ExxonMobil Bicor™ 25MB668 OPP Film

Category	Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade
Manufacturer	Exxon Chemical
Trade Name	Bicor™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	ExxonMobil Bicor™ 25MB668 OPP Film.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Product Description: A high speed transparent, biaxially oriented polypropylene film, coated one side acrylic, one side very low seal temperature (VLTS) coating. VLTS coating provides excellent performances on high speed HFFS machines. Acrylic coating provides aroma barrier and excellent support for printing.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Exceptional wide sealing range with a low minimum seal temperature (MST)Excellent seal strength and Hot-tackRobust performance on horizontal flowpack machinesExcellent humidity seal retention on VLTS sideGood aroma barrierOutstanding optical propertiesIdeal support for normal ink systemsWater-based coatingsFeatures:Acrylic CoatedFlavor & Aroma BarrierHumidity ResistantVery Broad Seal RangeVLTS CoatedApplications:BakeryBiscuits/Cookie/Crackers Confectionery, Chocolate Confectionery, Gum Confectionery, SugarFrozen FoodHealth and Beauty CareHealth and Beauty CareHousehold and Detergents Ice Cream Uses:HFFS Flexible Packaging Processing Method: Inner Web Adhesive Lamination, Solvent Rotogravure Printing and Surface Print UnsupportedInformation provided by ExxonMobil

Physical Properties	Metric	English	Comments
Water Vapor Transmission	1.10 g/m²/day @Temperature 23.0 °C	0.0710 g/100 in²/day @Temperature 73.4 °F	85% RH; ExxonMobil Method
	4.97 g/m²/day @Temperature 38.0 °C	0.320 g/100 in²/day @Temperature 100 °F	90% RH; ExxonMobil Method
Oxygen Transmission Rate	850 cc/m²/day @Temperature 23.0 °C	54.8 cc/100 in²/day @Temperature 73.4 °F	Wet, 75% RH; ExxonMobil Method
	854 cc/m²/day @Temperature 23.0 °C	55.0 cc/100 in²/day @Temperature 73.4 °F	0% RH; ExxonMobil Method
Thickness	24.9 microns	0.980 mil	ExxonMobil Method
Coating Weight	22.2 g/m²	13.9 lb/ream	ExxonMobil Method

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	175 %	175 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Elongation at Break, TD	60 %	60 %	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Modulus of Elasticity	2.00 GPa	290 ksi	MD; ExxonMobil Method
	3.80 GPa	551 ksi	TD; ExxonMobil Method
Coefficient of Friction	0.25	0.25	Acrylic; ExxonMobil Method
	0.40	0.40	VLTS; ExxonMobil Method
Seal Strength	410 g/25 mm @Pressure 0.138 MPa, Temperature 80.0 °C	410 g/in @Pressure 20.0 psi, Temperature 176 °F	LTS, 0.8 sec; ExxonMobl Method
Film Tensile Strength at Break, MD	160 MPa	23200 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method
Film Tensile Strength at Break, TD	290 MPa	42100 psi	7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method

Thermal Properties	Metric	English	Comments
Shrinkage, MD	6.0 % @Temperature 135 °C, Time 432 sec	6.0 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method
Shrinkage, TD	5.5 % @Temperature 135 °C, Time 432 sec	5.5 % @Temperature 275 °F, Time 0.120 hour	ExxonMobil Method

Optical Properties	Metric	English	Comments
Haze	1.2 %	1.2 %	ExxonMobil Method
Gloss	87 %	87 %	45°; ExxonMobil Method

Descriptive Properties	Value	Comments
Heat Seal Range	126°F	VLTS, 36.3 psi, 0.2 sec
Yield	31100 in²/lb