ExxonMobil Bicor™ 20MB080 OPP Film
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene, Film Grade |
| Manufacturer | Exxon Chemical |
| Trade Name | Bicor™ |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | ExxonMobil Bicor™ 20MB080 OPP Film.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Product Description: Bicor 20NB080 is a biaxially oriented polypropylene film metallizable on one side, with a heat sealable surface on the other side. Designed to be used after metallization as a single web in HFFS applications or in laminations for other purposes.Availability: Africa & Middle East, Asia Pacific and EuropeKey Features:Good adhesion layer for metallizationExcellent processability in metallizationGood machinability on HFFS machineVery good hot tackOne side sealableHigh yieldBrilliant metal appearance after metallizationFeatures:In Lamination Lap SealableApplications:IndustrialInformation provided by ExxonMobil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Water Vapor Transmission | 1.40 g/m²/day @Temperature 23.0 °C |
0.0900 g/100 in²/day @Temperature 73.4 °F |
85% RH; ExxonMobil Method |
| 6.98 g/m²/day @Temperature 38.0 °C |
0.450 g/100 in²/day @Temperature 100 °F |
90% RH; ExxonMobil Method | |
| Thickness | 20.1 microns | 0.790 mil | ExxonMobil Method |
| Coating Weight | 17.9 g/m² | 11.2 lb/ream | ExxonMobil Method |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Film Elongation at Break, MD | 175 % | 175 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Elongation at Break, TD | 60 % | 60 % | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Modulus of Elasticity | 2.00 GPa | 290 ksi | MD; ExxonMobil Method |
| 3.60 GPa | 522 ksi | TD; ExxonMobil Method | |
| Coefficient of Friction | 0.65 | 0.65 | Treated Surface; ExxonMobil Method |
| 0.85 | 0.85 | Untreated Surface; ExxonMobil Method | |
| Seal Strength | 460 g/25 mm @Pressure 0.276 MPa, Temperature 140 °C |
460 g/in @Pressure 40.0 psi, Temperature 284 °F |
Otto Bruger, 0.2 sec; ExxonMobl Method |
| Film Tensile Strength at Break, MD | 150 MPa | 21800 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Film Tensile Strength at Break, TD | 290 MPa | 42100 psi | 7.9 in/min, 4.9 in Jaw Separation; ExxonMobil Method |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage, MD | 6.5 % @Temperature 135 °C, Time 432 sec |
6.5 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Shrinkage, TD | 4.5 % @Temperature 135 °C, Time 432 sec |
4.5 % @Temperature 275 °F, Time 0.120 hour |
ExxonMobil Method |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Haze | 1.9 % | 1.9 % | ExxonMobil Method |
| Gloss | 85 % | 85 % | 45°; ExxonMobil Method |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Heat Seal Range | 54°F | 36.3 psi, 0.2 sec |
| Yield | 38600 in2/lb |
Users viewing this material also viewed the following:
- FKuR Kunststoff Bio-Flex® S 9533 Compostable PLA Blend
- Techmer ES Plastiblend® PA6 GF30 RM BK Nylon 6
- Chase Plastics CP Pryme® NNN260L (Dry) Nylon 66/6 Copolymer, 60% Glass Fiber Reinforced
- A. Schulman FORMION™ FI 342 Ionomer
- Zell-Metall Engineering Plastics Zellamid 1400 (PET) at 50% RH
- Covestro Bayblend® T 88-4N Polycarbonate/ABS Blend, 20% Glass Fiber
- ChevronTexaco Aquagear® EP 320
- Amco Amalloy® B9714 Polymer Alloy
- Aremco Crystalbond™ 555 Washaway Mounting Adhesive & Accessory
- Hexcel® HexPly® M56 180°C (350°F) Out-of-Autoclave Curing Matrix, M56/37%/280H5/AS4-3K
Copyright © lookpolymers.com All Rights Reserved