DuPont Teijin Films Melinex® SWC Polyester Film, 400 Gauge

Category	Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer	DuPont Teijin Films (DTF)
Trade Name	Melinex®
Port	Ningbo port,China
Trade Terms	EXW, FOB, CFR, CIF
Payment Terms	L/C, T/T, PayPal
Download PDF	DuPont Teijin Films Melinex® SWC Polyester Film, 400 Gauge.pdf
Price	EMAIL US sales@lookpolymers.com

Material Notes:

A narrow width film with consistently good handling properties; transparent in thin gauges, slightly hazy in thick gauges, ideally suited for wire and cable wrapping and insulation.Information provided by DuPont.

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	103 MPa	15000 psi	ASTM D882A
Film Tensile Strength at Yield, TD	103 MPa	15000 psi	ASTM D882A
Coefficient of Friction, Dynamic	0.40	0.40	A-B; ASTM D1894
Film Tensile Strength at Break, MD	193 MPa	28000 psi	ASTM D882A
Film Tensile Strength at Break, TD	221 MPa	32000 psi	ASTM D882A

Thermal Properties	Metric	English	Comments
Shrinkage, MD	3.0 % <br>@Temperature 190 °C,<br> Time 300 sec	3.0 % <br>@Temperature 374 °F,<br> Time 0.0833 hour	Unrestrained
Shrinkage, TD	1.0 % <br>@Temperature 190 °C,<br> Time 300 sec	1.0 % <br>@Temperature 374 °F,<br> Time 0.0833 hour	Unrestrained

Electrical Properties	Metric	English	Comments
Volume Resistivity	1.00e+17 ohm-cm <br>@Temperature 25.0 °C	1.00e+17 ohm-cm <br>@Temperature 77.0 °F	100 V DC 50% RH 1000 sec electrification time; ASTM D257
Surface Resistivity per Square	1.00e+15 ohm <br>@Temperature 25.0 °C	1.00e+15 ohm <br>@Temperature 77.0 °F	500 V DC @ 50% RH; ASTM D257
Dielectric Strength	132.9 kV/mm	3375 kV/in	1/4" electrode 500 V/sec 25°C in air; ASTM D149
Dielectric Breakdown	13500 V	13500 V	1/4" electrode 500 V/sec 25°C in air; ASTM D149
Dissipation Factor	0.0030 <br>@Frequency 100 Hz,<br> Temperature 25.0 °C	0.0030 <br>@Frequency 100 Hz,<br> Temperature 77.0 °F	ASTM D150
	0.055 <br>@Frequency 1000 Hz,<br> Temperature 25.0 °C	0.055 <br>@Frequency 1000 Hz,<br> Temperature 77.0 °F	ASTM D150