DuPont Teijin Films Melinex® 505 Polyester Film

Category Polymer , Film , Thermoplastic , Polyester, TP , Polyester Film
Manufacturer DuPont Teijin Films (DTF)
Trade Name Melinex®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Teijin Films Melinex® 505 Polyester Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Melinex® 505 is a high clarity polyester film which is pretreated on both sides to promote adhesion to most industrial coating and inks.Approvals: UL 94 VTM-2 - for 1000 gauge (0.26mm) onlyInformation provided by DuPont.
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 96.5 MPa
14000 psi
ASTM D882A
Film Tensile Strength at Yield, TD 96.5 MPa
14000 psi
ASTM D882A
Film Elongation at Break, MD 180 %
180 %
ASTM D882A
Film Elongation at Break, TD 105 %
105 %
ASTM D882A
Coefficient of Friction, Static 0.50
0.50
ASTM D1894
Film Tensile Strength at Break, MD 179 MPa
26000 psi
ASTM D882A
Film Tensile Strength at Break, TD 228 MPa
33000 psi
ASTM D882A
Thermal Properties Metric English Comments
Shrinkage, MD 2.5 %

@Temperature 190 °C,
Time 300 sec
2.5 %

@Temperature 374 °F,
Time 0.0833 hour
Unrestrained
Shrinkage, TD 1.0 %

@Temperature 190 °C,
Time 300 sec
1.0 %

@Temperature 374 °F,
Time 0.0833 hour
Unrestrained
Optical Properties Metric English Comments
Haze 0.30 %

@Thickness 0.0762 mm
0.30 %

@Thickness 0.00300 in
ASTM D1003
0.30 %

@Thickness 0.102 mm
0.30 %

@Thickness 0.00400 in
ASTM D1003
0.40 %

@Thickness 0.127 mm
0.40 %

@Thickness 0.00500 in
ASTM D1003
0.50 %

@Thickness 0.165 mm
0.50 %

@Thickness 0.00650 in
ASTM D1003
0.60 %

@Thickness 0.178 mm
0.60 %

@Thickness 0.00700 in
ASTM D1003
Transmission, Visible 87 %

@Thickness 0.178 mm
87 %

@Thickness 0.00700 in
TLT; ASTM D1003
87.2 %

@Thickness 0.165 mm
87.2 %

@Thickness 0.00650 in
TLT; ASTM D1003
88 %

@Thickness 0.127 mm
88 %

@Thickness 0.00500 in
TLT; ASTM D1003
88.3 %

@Thickness 0.102 mm
88.3 %

@Thickness 0.00400 in
TLT; ASTM D1003
88.5 %

@Thickness 0.0762 mm
88.5 %

@Thickness 0.00300 in
TLT; ASTM D1003