DuPont™ Sclairfilm® LWS-1 LMDPE Film, Laminating, 38.1 µm Thickness (discontinued **)

Category	Polymer , Film , Thermoplastic , Polyethylene (PE) , MDPE , Linear Medium Density Polyethylene (LMDPE), Film
Manufacturer
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont™ Sclairfilm® LWS-1 LMDPE Film, Laminating, 38.1 µm Thickness (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Data provided by DuPont Packaging Polymers.LWS is a linear medium density polyolefin film produced from Sclair® copolymer resin and designed primarily for laminating end uses. It is treated on one side for both ink and adhesive bonding properties. For laminating to other substrates such as Dartek® nylon film or Mylar® polyester film for heat-in-bag or boil-in-bag applications.

Physical Properties	Metric	English	Comments
Density	0.929 g/cc	0.0336 lb/in³
Moisture Vapor Transmission	0.270 cc-mm/m²-24hr-atm	0.686 cc-mil/100 in²-24hr-atm	ASTM E96 Procedure E
Water Vapor Transmission	7.00 g/m²/day	0.451 g/100 in²/day	ASTM E96 Procedure E
Oxygen Transmission	133 cc-mm/m²-24hr-atm	338 cc-mil/100 in²-24hr-atm	or 3500 cc/m²-24hr-atm for the film. ASTM D3985

Mechanical Properties	Metric	English	Comments
Film Elongation at Break, MD	500 %	500 %	ASTM D882
Tensile Modulus	0.370 GPa	53.7 ksi	ASTM D882
Dart Drop Test	75.0 g	0.165 lb
Seal Strength	>= 1200 g/25 mm	>= 1200 g/in	Sentinel Sealer Test
Film Tensile Strength at Break, MD	38.0 MPa	5510 psi	ASTM D882

Optical Properties	Metric	English	Comments
Haze	6.0 %	6.0 %	ASTM D1003
Gloss	85 %	85 %	20°; ASTM D2457