DuPont Performance Polymers Zytel® HTN 53G50HSLR NC010 Polyphthalamide (PPA)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyphthalamide (PPA) , Polyphthalamide (PPA), 50% Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Zytel® HTN
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Zytel® HTN 53G50HSLR NC010 Polyphthalamide (PPA)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
50% Glass Reinforced High Performance Polyamide with Improved Impact and Stiffness Zytel HTN53G50HSLR NC010 is a 50% glass reinforced heat stabilized lubricated high performance polyamide resin developed for moderate temperature structural applicationsInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.59 g/cc
0.0574 lb/in³
DAM; ISO 1183
Linear Mold Shrinkage, Flow 0.0020 cm/cm
0.0020 in/in
DAM; ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0040 cm/cm
0.0040 in/in
DAM; ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 215 MPa
31200 psi
50%RH; ISO 527-1/-2
250 MPa
36300 psi
DAM; ISO 527-1/-2
Tensile Stress 12.67 MPa

@Strain 0.0900 %,
Temperature 0.000 °C
 1838 psi

@Strain 0.0900 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
13.51 MPa

@Strain 0.0900 %,
Temperature -20.0 °C
 1959 psi

@Strain 0.0900 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
14.93 MPa

@Strain 0.400 %,
Temperature 150 °C
 2165 psi

@Strain 0.400 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
15.94 MPa

@Strain 0.100 %,
Temperature 0.000 °C
 2312 psi

@Strain 0.100 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
16.26 MPa

@Strain 0.110 %,
Temperature 23.0 °C
 2358 psi

@Strain 0.110 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
17.84 MPa

@Strain 0.120 %,
Temperature 40.0 °C
 2587 psi

@Strain 0.120 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
17.96 MPa

@Strain 0.120 %,
Temperature -20.0 °C
 2605 psi

@Strain 0.120 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
18.1 MPa

@Strain 0.130 %,
Temperature 23.0 °C
 2630 psi

@Strain 0.130 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
20.09 MPa

@Strain 0.360 %,
Temperature 90.0 °C
 2914 psi

@Strain 0.360 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
21.04 MPa

@Strain 0.530 %,
Temperature 150 °C
 3052 psi

@Strain 0.530 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
25.66 MPa

@Strain 0.250 %,
Temperature 40.0 °C
 3722 psi

@Strain 0.250 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
29.88 MPa

@Strain 0.400 %,
Temperature 90.0 °C
 4334 psi

@Strain 0.400 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
32.77 MPa

@Strain 1.52 %,
Temperature 150 °C
 4753 psi

@Strain 1.52 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
40.98 MPa

@Strain 2.67 %,
Temperature 150 °C
 5944 psi

@Strain 2.67 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
45.0 MPa

@Strain 2.00 %,
Temperature 150 °C
 6530 psi

@Strain 2.00 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
46.47 MPa

@Strain 3.81 %,
Temperature 150 °C
 6740 psi

@Strain 3.81 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
49.0 MPa

@Strain 1.45 %,
Temperature 90.0 °C
 7110 psi

@Strain 1.45 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
55.95 MPa

@Strain 7.24 %,
Temperature 150 °C
 8115 psi

@Strain 7.24 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
56.17 MPa

@Strain 3.50 %,
Temperature 150 °C
 8147 psi

@Strain 3.50 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
56.72 MPa

@Strain 0.360 %,
Temperature 0.000 °C
 8227 psi

@Strain 0.360 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
58.41 MPa

@Strain 9.14 %,
Temperature 150 °C
 8472 psi

@Strain 9.14 %,
Temperature 302 °F
 50%RH; ISO 11403-1 -2
60.18 MPa

@Strain 0.360 %,
Temperature -20.0 °C
 8728 psi

@Strain 0.360 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
61.33 MPa

@Strain 2.53 %,
Temperature 90.0 °C
 8895 psi

@Strain 2.53 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
63.55 MPa

@Strain 4.96 %,
Temperature 150 °C
 9217 psi

@Strain 4.96 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
64.73 MPa

@Strain 0.400 %,
Temperature 0.000 °C
 9388 psi

@Strain 0.400 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
66.67 MPa

@Strain 0.410 %,
Temperature 23.0 °C
 9670 psi

@Strain 0.410 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
68.93 MPa

@Strain 3.62 %,
Temperature 90.0 °C
 9997 psi

@Strain 3.62 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
70.09 MPa

@Strain 0.490 %,
Temperature 23.0 °C
 10170 psi

@Strain 0.490 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
74.43 MPa

@Strain 0.480 %,
Temperature 40.0 °C
 10800 psi

@Strain 0.480 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
75.15 MPa

@Strain 1.54 %,
Temperature 90.0 °C
 10900 psi

@Strain 1.54 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
75.63 MPa

@Strain 0.470 %,
Temperature -20.0 °C
 10970 psi

@Strain 0.470 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
76.16 MPa

@Strain 9.43 %,
Temperature 150 °C
 11050 psi

@Strain 9.43 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
77.63 MPa

@Strain 1.00 %,
Temperature 40.0 °C
 11260 psi

@Strain 1.00 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
78.59 MPa

@Strain 11.92 %,
Temperature 150 °C
 11400 psi

@Strain 11.92 %,
Temperature 302 °F
 DAM; ISO 11403-1 -2
79.81 MPa

@Strain 6.86 %,
Temperature 90.0 °C
 11580 psi

@Strain 6.86 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
81.52 MPa

@Strain 8.65 %,
Temperature 90.0 °C
 11820 psi

@Strain 8.65 %,
Temperature 194 °F
 50%RH; ISO 11403-1 -2
96.68 MPa

@Strain 2.70 %,
Temperature 90.0 °C
 14020 psi

@Strain 2.70 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
96.82 MPa

@Strain 0.620 %,
Temperature 0.000 °C
 14040 psi

@Strain 0.620 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
103.7 MPa

@Strain 0.620 %,
Temperature -20.0 °C
 15040 psi

@Strain 0.620 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
104.54 MPa

@Strain 1.74 %,
Temperature 40.0 °C
 15162 psi

@Strain 1.74 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
108.99 MPa

@Strain 3.85 %,
Temperature 90.0 °C
 15808 psi

@Strain 3.85 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
109.97 MPa

@Strain 0.850 %,
Temperature 23.0 °C
 15950 psi

@Strain 0.850 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
110.4 MPa

@Strain 0.700 %,
Temperature 0.000 °C
 16010 psi

@Strain 0.700 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
110.75 MPa

@Strain 0.710 %,
Temperature 23.0 °C
 16063 psi

@Strain 0.710 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
120.98 MPa

@Strain 2.49 %,
Temperature 40.0 °C
 17547 psi

@Strain 2.49 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
122.53 MPa

@Strain 0.840 %,
Temperature 40.0 °C
 17772 psi

@Strain 0.840 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
124.67 MPa

@Strain 7.68 %,
Temperature 90.0 °C
 18082 psi

@Strain 7.68 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
125.6 MPa

@Strain 9.61 %,
Temperature 90.0 °C
 18220 psi

@Strain 9.61 %,
Temperature 194 °F
 DAM; ISO 11403-1 -2
128.32 MPa

@Strain 0.820 %,
Temperature -20.0 °C
 18611 psi

@Strain 0.820 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
131.89 MPa

@Strain 0.880 %,
Temperature 0.000 °C
 19129 psi

@Strain 0.880 %,
Temperature 32.0 °F
 50%RH; ISO 11403-1 -2
135.04 MPa

@Strain 5.96 %,
Temperature 40.0 °C
 19586 psi

@Strain 5.96 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
136.27 MPa

@Strain 4.72 %,
Temperature 40.0 °C
 19764 psi

@Strain 4.72 %,
Temperature 104 °F
 50%RH; ISO 11403-1 -2
138.36 MPa

@Strain 1.20 %,
Temperature 23.0 °C
 20067 psi

@Strain 1.20 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2
140.62 MPa

@Strain 0.880 %,
Temperature -20.0 °C
 20395 psi

@Strain 0.880 %,
Temperature -4.00 °F
 50%RH; ISO 11403-1 -2
148.68 MPa

@Strain 1.01 %,
Temperature 23.0 °C
 21564 psi

@Strain 1.01 %,
Temperature 73.4 °F
 DAM; ISO 11403-1 -2
153.08 MPa

@Strain 1.01 %,
Temperature 0.000 °C
 22202 psi

@Strain 1.01 %,
Temperature 32.0 °F
 DAM; ISO 11403-1 -2
160.11 MPa

@Strain 1.20 %,
Temperature 40.0 °C
 23222 psi

@Strain 1.20 %,
Temperature 104 °F
 DAM; ISO 11403-1 -2
176.84 MPa

@Strain 1.17 %,
Temperature -20.0 °C
 25649 psi

@Strain 1.17 %,
Temperature -4.00 °F
 DAM; ISO 11403-1 -2
183.62 MPa

@Strain 2.29 %,
Temperature 23.0 °C
 26632 psi

@Strain 2.29 %,
Temperature 73.4 °F
 50%RH; ISO 11403-1 -2