Dow SE SLR-4601 Solution polymerized Styrene Butadiene Rubber (S-SBR)

Category	Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE)
Manufacturer	Dow Chemical
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow SE SLR-4601 Solution polymerized Styrene Butadiene Rubber (S-SBR).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

SE SLR-4601 is manufactured by anionic solution polymerization using lithium initiator. It is a product with medium styrene and high vinyl content. The product is partially Sn-coupled and chemically modified. A non-staining stabilizer is added during the production process. SE SLR-4601 is widely used in the tire industry where an excellent balance between wet grip and rolling resistance is required. The material can also be used to manufacture high quality technical rubber articles. It is supplied in bales weighing 25 kg. Bales are wrapped in 50 micron PE film. At mixing temperatures above 110°C, the rubber can be processed with the packaging film. Information provided by Dow

Physical Properties	Metric	English	Comments
Viscosity Measurement	1.9 @Temperature 160 °C	1.9 @Temperature 320 °F	[dNm]; ML, (0.5 RAD); ASTM D5289
	4.5 @Temperature 160 °C	4.5 @Temperature 320 °F	[min]; ts1, (0.5 RAD); ASTM D5289
	6.5 @Temperature 160 °C	6.5 @Temperature 320 °F	[min]; T50, (0.5 RAD); ASTM D5289
	12 @Temperature 160 °C	12 @Temperature 320 °F	[min]; T90, (0.5 RAD); ASTM D5289
	16.9 @Temperature 160 °C	16.9 @Temperature 320 °F	[dNm]; MH, (0.5 RAD); ASTM D5289
Mooney Viscosity	50 @Temperature 100 °C	50 @Temperature 212 °F	[MU]; ML 1+4, massed sample; ASTM D1646
Vinyl Acetate Content	63 %	63 %	FTIR, internal method
Collected Volatile Condensable Material	0.15 %	0.15 %	ASTM D5668
Storage Temperature	<= 30.0 °C	<= 86.0 °F

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	61.5 @Thickness 12.5 mm	61.5 @Thickness 0.492 in	(25 min / 160°C); ASTM D2240
Tensile Strength, Ultimate	19.0 MPa	2760 psi	Die C (35 min / 145°C); ASTM D412
Tensile Strength, Yield	15.0 MPa @Strain 300 %	2180 psi @Strain 300 %	ASTM D412
Elongation at Break	350 %	350 %	ASTM D412
Rebound	24.5 % @Thickness 12.5 mm	24.5 % @Thickness 0.492 in	Schob pendulum, (25 min / 160°C); ISO 4662

Thermal Properties	Metric	English	Comments
Vicat Softening Point	92.2 °C	198 °F
Glass Transition Temp, Tg	-25.0 °C	-13.0 °F	HR 10 K/min; half height; DSC

Chemical Properties	Metric	English	Comments
Styrene Content	21 %	21 %	FTIR, internal method

Processing Properties	Metric	English	Comments
Shelf Life	>= 12.0 Month	>= 12.0 Month

Descriptive Properties	Value	Comments
Accelerator (CBS) wt%	1
Aromatic Oil wt%	5
Carbon Black wt%	50	; IRB 7
Stearic Acid wt%	1.5
Sulfur content, %	1.75
Zinc Oxide wt%	3