Dow ATTANE™ 4201G, 0.8mil Ultra Low Density Ethylene/Octene Copolymer

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Dow Chemical
Trade Name ATTANE™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow ATTANE™ 4201G, 0.8mil Ultra Low Density Ethylene/Octene Copolymer.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ATTANE™ 4201G is used for packaging applications. It offers toughness, seal properties, optical properties and processability. It complies with U.S. FDA 21 CFR 177.1520 (c) 3.2a.Information provided by Dow
Physical Properties Metric English Comments
Density 0.912 g/cc
0.0329 lb/in³
ASTM D792
Oxygen Transmission 282 cc-mm/m²-24hr-atm
716 cc-mil/100 in²-24hr-atm
ASTM D3985
Thickness 20.3 microns
0.800 mil
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.832 MPa
1426 psi
ASTM D882
Film Tensile Strength at Yield, TD 8.956 MPa
1299 psi
ASTM D882
Film Elongation at Break, MD 464 %
464 %
ASTM D882
Film Elongation at Break, TD 691 %
691 %
ASTM D882
Secant Modulus, MD 0.128 GPa
18.6 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.144 GPa
20.9 ksi
2% Secant; ASTM D882
Impact 295
295
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
Elmendorf Tear Strength MD 326 g
326 g
ASTM D1922
Elmendorf Tear Strength TD 533 g
533 g
ASTM D1922
Elmendorf Tear Strength, MD 16.04 g/micron
407.5 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 26.230 g/micron
666.25 g/mil
ASTM D1922
Dart Drop Test 449 g
0.990 lb
Method B; ASTM D1709
Film Tensile Strength at Break, MD 49.01 MPa
7108 psi
ASTM D882
Film Tensile Strength at Break, TD 45.26 MPa
6565 psi
ASTM D882
Heat Seal Strength Initiation Temperature 95.0 °C
203 °F
1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
Thermal Properties Metric English Comments
Melting Point 123 °C
253 °F
Dow Method (DSC)
Vicat Softening Point 93.0 °C
199 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 8.0 %
8.0 %
ASTM D1003
Gloss 67 %
67 %
45°; ASTM D2457
Transmission, Visible 97 %
97 %
Clarity; ASTM D1746