Chosun Refractories SFC-90W High-Alumina Castable
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories SFC-90W High-Alumina Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.017658 GPa @Temperature 110 °C, Time 86400 sec |
2.5611 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.023544 GPa @Temperature 1000 °C, Time 10800 sec |
3.4148 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| 0.024525 GPa @Temperature 1400 °C, Time 10800 sec |
3.5571 ksi @Temperature 2550 °F, Time 3.00 hour |
||
| Compressive Strength | 98.1 MPa @Temperature 110 °C, Time 86400 sec |
14200 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 108 MPa @Temperature 1000 °C, Time 10800 sec |
15600 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 113 MPa @Temperature 1400 °C, Time 10800 sec |
16400 psi @Temperature 2550 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Maximum Service Temperature, Air | 1800 °C | 3270 °F | limited |
| Shrinkage | -0.350 % @Temperature 1400 °C, Time 10800 sec |
-0.350 % @Temperature 2550 °F, Time 3.00 hour |
|
| -0.100 % @Temperature 1000 °C, Time 10800 sec |
-0.100 % @Temperature 1830 °F, Time 3.00 hour |
||
| -0.0300 % @Temperature 110 °C, Time 86400 sec |
-0.0300 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 95 % | 95 % | |
| SiO2 | 4.0 % | 4.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Self Flowing | |
| Material Required for Estimating(kg/?) | 3,200 | |
| Water Required for Casting(%) | 5-5.5 |
Users viewing this material also viewed the following:
- Rogers Corporation Bisco™ HT-820 Cellular Silicone Foam
- Albis Plastics Cellulose Acetate Butyrate B900 (Base Grade), 7% Plasticizer (discontinued **)
- Mitsubishi Iupilon® S2001R 9.5 MFI FDA Compliant Polycarbonate With Release
- Gwent Electronic Materials D50706P3 Polymer Dielectric
- Techmer ES HiFill® PA6 GF50 RM LE 50% Glass Filled (Conditioned)
- ChevronTexaco ECO® SAE 30 Heavy Duty Motor Oil
- ExxonMobil Mobiltrans AST
- Arlon 51991A020 0.020" (0.508 mm) Uncured Silicone Rubber with Fiberglass Substrate
- DuPont Performance Polymers Sorona® 3015G BK001 Polytrimethylene Terephthalate (PTT) (Unverified Data**)&
- A. Schulman POLYBLAK™ 3422 Black Color Concentrate, 35% Carbon Black Based In LDPE
Copyright © lookpolymers.com All Rights Reserved