Chosun Refractories INCT-160 Light-Weight Castable
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories INCT-160 Light-Weight Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 4.33e-7 - 0.00147 GPa @Temperature 110 °C, Time 86400 sec |
0.0000628 - 0.213 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0014715 - 0.0044145 GPa @Temperature 1000 °C, Time 10800 sec |
0.21343 - 0.64028 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| 0.002943 - 0.005886 GPa @Temperature 1350 °C, Time 10800 sec |
0.4269 - 0.8537 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| Compressive Strength | 4.90 - 14.7 MPa @Temperature 110 °C, Time 86400 sec |
711 - 2130 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 4.90 - 14.7 MPa @Temperature 1000 °C, Time 10800 sec |
711 - 2130 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 9.81 - 19.6 MPa @Temperature 1350 °C, Time 10800 sec |
1420 - 2840 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.60484 W/m-K @Temperature 260 °C |
4.1908 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.66300 W/m-K @Temperature 540 °C |
4.5938 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 0.72115 W/m-K @Temperature 800 °C |
4.9967 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1600 °C | 2910 °F | limited |
| Shrinkage | -0.0500 % @Temperature 1000 °C, Time 10800 sec |
-0.0500 % @Temperature 1830 °F, Time 3.00 hour |
|
| -0.0300 % @Temperature 110 °C, Time 86400 sec |
-0.0300 % @Temperature 230 °F, Time 24.0 hour |
||
| 0.050 % @Temperature 1350 °C, Time 10800 sec |
0.050 % @Temperature 2460 °F, Time 3.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 63 % | 63 % | |
| SiO2 | 28 % | 28 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Main Applications | High temperature furnaces | |
| Material Required for Estimating (kg/?) | 1,500 | |
| Water Required for Casting(%) | 20-25 |
Users viewing this material also viewed the following:
- SABIC PP 413MNK45 Polypropylene Impact Copolymer for Injection Molding
- NIZHNEKAMSKNEFTEKHIM PE 2062U (62111) High Density Polyethylene
- SABIC Innovative Plastics Lexan® IR2040 PC (Europe-Africa-Middle East)
- GRECO ISOTHANE 3080AF Polyether TPU Resin
- Lucas-Milhaupt Silvaloy® 30 Brazing Alloy
- Samsung Cheil Industries Infino® AR-9301 PA, Glass Filled General Purpose
- 3M Cushion-Mount™ E1840H Plus Plate Mounting Tapes with Easy Mount Adhesive and High Plateside Adhesion
- Aaron Industries AAROLENE® ARPP 200-2 PP Black Polypropylene Copolymer
- Lucite International Series 500 Liquid Acrylic Resin
Copyright © lookpolymers.com All Rights Reserved