Chosun Refractories INCT-140 Light-Weight Castable
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories INCT-140 Light-Weight Castable.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 4.33e-7 - 0.00147 GPa @Temperature 110 °C, Time 86400 sec |
0.0000628 - 0.213 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0014715 - 0.0044145 GPa @Temperature 500 °C, Time 10800 sec |
0.21343 - 0.64028 ksi @Temperature 932 °F, Time 3.00 hour |
||
| 0.0014715 - 0.0044145 GPa @Temperature 1000 °C, Time 10800 sec |
0.21343 - 0.64028 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| Compressive Strength | 4.90 - 14.7 MPa @Temperature 110 °C, Time 86400 sec |
711 - 2130 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 4.90 - 14.7 MPa @Temperature 500 °C, Time 10800 sec |
711 - 2130 psi @Temperature 932 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 4.90 - 14.7 MPa @Temperature 1000 °C, Time 10800 sec |
711 - 2130 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.3955 W/m-K @Temperature 260 °C |
2.740 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.44200 W/m-K @Temperature 540 °C |
3.0625 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 0.48852 W/m-K @Temperature 800 °C |
3.3849 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1400 °C | 2550 °F | limited |
| Shrinkage | -0.250 % @Temperature 1000 °C, Time 10800 sec |
-0.250 % @Temperature 1830 °F, Time 3.00 hour |
|
| -0.0600 % @Temperature 110 °C, Time 86400 sec |
-0.0600 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 50 % | 50 % | |
| SiO2 | 36 % | 36 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Main Applications | Fireproof insulating castable | |
| Material Required for Estimating (kg/?) | 1,350 | |
| Water Required for Casting(%) | 25-30 |
Users viewing this material also viewed the following:
- Ravago Manufacturing Americas Hylon® N2040MHL Nylon 6 (DAM)
- DuPont™ Surlyn® 8120 Ionomer Resin, Sodium (discontinued **)
- SABIC Innovative Plastics Valox® IQ357 PBT+PC (Europe-Africa-Middle East)
- Washington Penn Medium Impact Copolymer 40% Calcium Carbonate Filled
- Daikin POLYFLON MG-1030F PTFE 15% Glass Fiber Filled Molding Powder, High Apparent Density, Free Flow
- Aclo Accucomp Polyacetal (POM) ACE093L Low Viscosity
- 3M 444PC Double Coated Tapes with Adhesive 300
- BLUESTAR 201G25 PBT, 25% Glass Filled
- Arlon R34020W062 0.062" (1.57 mm) Uncured, Unsupported Silicone Rubber on a Kodacel Carrier
Copyright © lookpolymers.com All Rights Reserved