Chosun Refractories CT-140 Fireclay Castables
| Category | Ceramic , Oxide , Silicon Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories CT-140 Fireclay Castables.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.001962 - 0.005886 GPa @Temperature 110 °C, Time 86400 sec |
0.2846 - 0.8537 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.001962 - 0.005886 GPa @Temperature 1000 °C, Time 10800 sec |
0.2846 - 0.8537 ksi @Temperature 1830 °F, Time 3.00 hour |
||
| 0.0024525 - 0.0063765 GPa @Temperature 1350 °C, Time 10800 sec |
0.35571 - 0.92485 ksi @Temperature 2460 °F, Time 3.00 hour |
||
| Compressive Strength | 9.81 - 19.6 MPa @Temperature 110 °C, Time 86400 sec |
1420 - 2840 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 9.81 - 19.6 MPa @Temperature 1000 °C, Time 10800 sec |
1420 - 2840 psi @Temperature 1830 °F, Time 3.00 hour |
Cold Crushing Strength | |
| 9.81 - 19.6 MPa @Temperature 1350 °C, Time 10800 sec |
1420 - 2840 psi @Temperature 2460 °F, Time 3.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.60484 W/m-K @Temperature 260 °C |
4.1908 BTU-in/hr-ft²-°F @Temperature 500 °F |
|
| 0.68626 W/m-K @Temperature 540 °C |
4.7549 BTU-in/hr-ft²-°F @Temperature 1000 °F |
||
| 0.73279 W/m-K @Temperature 800 °C |
5.0773 BTU-in/hr-ft²-°F @Temperature 1470 °F |
||
| Maximum Service Temperature, Air | 1400 °C | 2550 °F | limited |
| Shrinkage | -0.300 % @Temperature 1350 °C, Time 10800 sec |
-0.300 % @Temperature 2460 °F, Time 3.00 hour |
|
| -0.0900 % @Temperature 110 °C, Time 86400 sec |
-0.0900 % @Temperature 230 °F, Time 24.0 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 36 % | 36 % | |
| SiO2 | 54 % | 54 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Installation Method | Casting, Troweling | |
| Material Required for Estimating(kg/?) | 1,850 | |
| Water Required for Casting(%) | 13.0 |
Users viewing this material also viewed the following:
- Nye Lubricants UniFlor 8511U (UF) Synthetic Oil
- Total Lacqrene® 3351(AS) Impact Polystyrene (discontinued **)
- Gwent Electronic Materials C2040712D5 Ink Jet Printable Silver Ink
- Hexcel® HexWeb® HRH-10 - 3/16 - 4.0 Aramid Fiber/Phenolic Resin Honeycomb
- California Fine Wire Copper Clad 1006 Steel (40% Conductivity)
- BASF Neopolen® P 9335 MG 0.04 g/cc Core density; Expanded Polypropylene (Europe)
- DuPont Performance Polymers Zytel® 73G45L NC010 Nylon 6 (Unverified Data**)
- SABIC Innovative Plastics LNP THERMOTUF IX02582 PA 6/12 (Asia Pacific)
- EG85A-B20 Polyurethane-based Biomedical Elastomer
Copyright © lookpolymers.com All Rights Reserved