Chosun Refractories AU3 Blast Furnace Runner Refractory
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | Chosun Refractories |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Chosun Refractories AU3 Blast Furnace Runner Refractory.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Chosun Refractories via Korea Institute of Ceramic Engineering and Technology (KICET).
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Bulk Density | 2.64 g/cc @Temperature 1450 °C, Time 7200 sec |
0.0954 lb/in³ @Temperature 2640 °F, Time 2.00 hour |
|
| 2.70 g/cc @Temperature 110 °C, Time 86400 sec |
0.0975 lb/in³ @Temperature 230 °F, Time 24.0 hour |
||
| Porosity | 16.3 % @Temperature 110 °C, Time 86400 sec |
16.3 % @Temperature 230 °F, Time 24.0 hour |
|
| 21.2 % @Temperature 1450 °C, Time 7200 sec |
21.2 % @Temperature 2640 °F, Time 2.00 hour |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Modulus of Rupture | 0.0026487 GPa @Temperature 110 °C, Time 86400 sec |
0.38417 ksi @Temperature 230 °F, Time 24.0 hour |
|
| 0.0080442 GPa @Temperature 1450 °C, Time 10800 sec |
1.1667 ksi @Temperature 2640 °F, Time 3.00 hour |
||
| Compressive Strength | 10.6 MPa @Temperature 110 °C, Time 86400 sec |
1540 psi @Temperature 230 °F, Time 24.0 hour |
Cold Crushing Strength |
| 30.4 MPa @Temperature 1450 °C, Time 7200 sec |
4410 psi @Temperature 2640 °F, Time 2.00 hour |
Cold Crushing Strength |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Shrinkage | -0.0700 % @Temperature 1450 °C, Time 7200 sec |
-0.0700 % @Temperature 2640 °F, Time 2.00 hour |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 55 % | 55 % | |
| SiC | 35 % | 35 % | |
| SiO2 | 5.0 % | 5.0 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Chemical Analysis(%),FC | 2 | |
| Installation Method | Casing Vibration | |
| Main Applications | Main runner Metal Zone | |
| Material Required for Estimating (kg/?) | 2,740 | |
| Water Required for Casting(%) | 6.5 |
Users viewing this material also viewed the following:
- Kennametal Stellite Deloro® 29 Nickel Alloy
- Inno-Comp INNOPOL® CS 2-9514 10% Talc-Filled, Elastomer Modified Polypropylene Block-Copolymer
- Ineos ABS Lustran® SMA 2171 SMA, Injection Molding Grade
- A. Schulman PP 3487-01 Polypropylene Homopolymer Polypropylene
- Fainplast Compounds Hax™ HFX 521 Crosslinkable HFFR Cable Compound
- ATI Allegheny Ludlum Altemp® X-750 Nickel-Based superalloy
- Bisalloy Steels BisPlate 400 Thickness 16-80 mm
- DSM Arnitel® UM551 Polyether Ester Elastomer (European Grade)
Copyright © lookpolymers.com All Rights Reserved