- CeramTec V 38 Alumina, 96.0% Al2O3-SiO2
CeramTec V 38 Alumina, 96.0% Al2O3-SiO2
| Category | Ceramic , Oxide , Aluminum Oxide |
| Manufacturer | CeramTec North America |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | CeramTec V 38 Alumina, 96.0% Al2O3-SiO2.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Aluminas exhibit good mechanical properties such as hardness, compressive and tensile strength, and elastic modulus. They perform well at elevated temperatures.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 3.75 g/cc | 0.135 lb/in³ | DIN EN 623-2 |
| Water Absorption | 0.00 % | 0.00 % | Open Porosity; DIN EN 623-2 |
| Permeability | 0.00 | 0.00 | %, Gas |
| Weibull Modulus | 13 | 13 | DINV ENV 843-5 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Vickers Microhardness | 1620 | 1620 | HV1; DINV ENV 843-4 |
| Tensile Modulus | 350 GPa | 50800 ksi | Young's; DINV ENV 843-2 |
| Flexural Strength | 310 MPa | 45000 psi | DIN EN 843-1 |
| Compressive Strength | 2500 MPa | 363000 psi | DIN 51067T1 |
| Poissons Ratio | 0.23 | 0.23 | DINV ENV 843-2 |
| Fracture Toughness | 4.00 MPa-m½ | 3.64 ksi-in½ | K<sub>IC</sub> (SEVNB); DIN CEN/TS 14425-1 |
| Shear Modulus | 142 GPa | 20600 ksi | Calculated |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear | 7.60 µm/m-°C @Temperature 20.0 - 400 °C |
4.22 µin/in-°F @Temperature 68.0 - 752 °F |
DIN EN 821-1 |
| 8.80 µm/m-°C @Temperature 20.0 - 1000 °C |
4.89 µin/in-°F @Temperature 68.0 - 1830 °F |
DIN EN 821-1 | |
| Specific Heat Capacity | 0.900 J/g-°C | 0.215 BTU/lb-°F | DINV ENV 821-3 |
| Thermal Conductivity | 20.0 W/m-K | 139 BTU-in/hr-ft²-°F | DIN EN 821-2 |
| Maximum Service Temperature, Air | 1200 °C | 2190 °F | |
| Maximum Service Temperature, Inert | 1200 °C | 2190 °F |
| Component Elements Properties | Metric | English | Comments |
|---|---|---|---|
| Al2O3 | 96 % | 96 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+8 ohm-cm @Temperature 400 °C |
1.00e+8 ohm-cm @Temperature 752 °F |
IEC 672-1 |
| 1.00e+15 ohm-cm @Temperature 20.0 °C |
1.00e+15 ohm-cm @Temperature 68.0 °F |
IEC 672-1 | |
| Dielectric Constant | 8.0 @Frequency 1.00e+6 Hz |
8.0 @Frequency 1.00e+6 Hz |
IEC 672-1 |
| Dielectric Strength | 17.0 kV/mm | 432 kV/in | IEC 672-1 |
| Dielectric Loss Index | 0.0050 @Frequency 9.00e+9 Hz |
0.0050 @Frequency 9.00e+9 Hz |
IEC 672-1 |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Ra = Arithmetic Mean Roughness Value (µm) | <0.15 | |
| Thermal Shock Resistance R1 (K) | 96 | calculated; R1 = [s? (1-µ)] / (a·E) |
Users viewing this material also viewed the following:
- PolyOne OnForce™ LFT NN-40LGF/000 HS Natural Polyamide 66 (Nylon 66)
- NYC YT3CP Y2O3 Powder
- SABIC Innovative Plastics Lexan® ML6411 PC Copolymer (Europe-Africa-Middle East)
- 3M Dyneon™ Fluorel™ FC-2179 Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- DuPont Performance Polymers Crastin® ST820 BK503 PBT (Unverified Data**)
- Solvay Specialty Polymers Cogegum® GFR/365 Polyolefin, Unspecified (Unverified Data**)
- LNP Lubricomp® EL-4030 Polyetherimide, PTFE Additive (discontinued **)
- Techmer ES Elastoblend® PA6 GF15 IM L 15% Glass Filled
- Eurostar Star X 1615 33V S4 PA66, Glass Fiber Reinforced, UV stabilized, Injection Molding
- ATI Allvac® Nickelvac® X-750 Nickel Superalloy, Heat Treatment: 1149°C (2100°F) + Age
Copyright © lookpolymers.com All Rights Reserved