BNZ Materials PA 26 Insulating Firebrick

Category	Ceramic , Oxide , Silicon Oxide
Manufacturer	BNZ Materials, Inc.
Trade Name
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BNZ Materials PA 26 Insulating Firebrick.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

BNZ produces many types of Insulating Fire Brick (IFB) for use in applications from 2,000°F (1,093°C) to 3,200°F (1,760°C). Each type is formulated to meet specific thermal and physical requirements and after firing is machined to precise tolerances. Made from high purity refractory clays and other ceramic raw materials, these IFB contain a carefully graded organic filler which is burned out during manufacture to give a uniform controlled pore structure.Information provided by BNZ Materials Inc.

Physical Properties	Metric	English	Comments
Density	0.785 g/cc	0.0284 lb/in³	ASTM C134
Deformation	-0.200 % @Temperature 1204 °C, Time 5400 sec	-0.200 % @Temperature 2199 °F, Time 1.50 hour	10 psi load, Hot Load Strength; ASTM C16

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.00124 GPa	0.180 ksi
Compressive Strength	1.67 MPa	242 psi	Cold Crush Strength

Thermal Properties	Metric	English	Comments
CTE, linear	5.60 µm/m-°C @Temperature 20.0 - 1093 °C	3.11 µin/in-°F @Temperature 68.0 - 1999 °F
Thermal Conductivity	0.300 W/m-K @Temperature 260 °C	2.08 BTU-in/hr-ft²-°F @Temperature 500 °F	ASTM C182
	0.350 W/m-K @Temperature 538 °C	2.43 BTU-in/hr-ft²-°F @Temperature 1000 °F	ASTM C182
	0.390 W/m-K @Temperature 816 °C	2.71 BTU-in/hr-ft²-°F @Temperature 1500 °F	ASTM C182
	0.420 W/m-K @Temperature 1093 °C	2.91 BTU-in/hr-ft²-°F @Temperature 1999 °F	ASTM C182
Maximum Service Temperature, Air	1427 °C	2601 °F
Shrinkage	0.10 % @Temperature 1399 °C, Time 86400 sec	0.10 % @Temperature 2550 °F, Time 24.0 hour	Permanent Linear Change; ASTM C210

Component Elements Properties	Metric	English	Comments
Al2O3	40.1 %	40.1 %
CaO	0.30 %	0.30 %
Fe2O3	0.70 %	0.70 %
MgO	0.10 %	0.10 %
Na2O	0.40 %	0.40 %	Includes K<sub>2</sub>O
SiO2	57 %	57 %
TiO2	1.5 %	1.5 %