BNZ Materials Blazecrete 2600 Dense Castable

Category	Ceramic , Oxide
Manufacturer	BNZ Materials, Inc.
Trade Name	Blazecrete
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BNZ Materials Blazecrete 2600 Dense Castable.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Blazecrete 2600 is a general purpose castable for service to 2600°F (1427°C). It is especially effective in casting door linings, boiler walls, monolithic car tops, hearths, fire boxes, as well as safety linings in continuous casting tundishes.Information provided by BNZ Materials Inc.

Physical Properties	Metric	English	Comments
Density	2.08 g/cc	0.0752 lb/in³

Mechanical Properties	Metric	English	Comments
Modulus of Rupture	0.00480 GPa	0.696 ksi	At Use Limit; ASTM C268
	0.000700 GPa @Temperature 815 °C	0.102 ksi @Temperature 1500 °F	ASTM C268
	0.000700 GPa @Temperature 1095 °C	0.102 ksi @Temperature 2003 °F	ASTM C268
	0.000900 GPa @Temperature 540 °C	0.131 ksi @Temperature 1000 °F	Fired; ASTM C268
	0.00140 GPa @Temperature 1260 °C	0.203 ksi @Temperature 2300 °F	ASTM C268
	0.00280 GPa @Temperature 104 °C	0.406 ksi @Temperature 219 °F	Dried; ASTM C268
	0.00410 GPa @Temperature 1371 °C	0.595 ksi @Temperature 2500 °F	ASTM C268
Compressive Strength	27.6 MPa	4000 psi	Cold Crush Strength
	6.90 MPa @Temperature 1095 °C	1000 psi @Temperature 2003 °F	Cold Crush Strength
	12.4 MPa @Temperature 815 °C	1800 psi @Temperature 1500 °F	Cold Crush Strength
	14.5 MPa @Temperature 1260 °C	2100 psi @Temperature 2300 °F	Cold Crush Strength
	14.5 MPa @Treatment Temp. 540 °C	2100 psi @Treatment Temp. 1000 °F	Cold Crush Strength; Dried 104°C
	17.9 MPa @Treatment Temp. 104 °C	2600 psi @Treatment Temp. 219 °F	Cold Crush Strength; Dried 104°C

Thermal Properties	Metric	English	Comments
Maximum Service Temperature, Air	1427 °C	2601 °F
Shrinkage	0.00 % @Temperature 104 °C	0.00 % @Temperature 219 °F	Permanent Linear Change; ASTM C210
	0.00 % @Temperature 540 °C	0.00 % @Temperature 1000 °F	Permanent Linear Change; ASTM C210
	0.00 % @Temperature 815 °C	0.00 % @Temperature 1500 °F	Permanent Linear Change; ASTM C210
	0.20 % @Temperature 1095 °C	0.20 % @Temperature 2003 °F	Permanent Linear Change; ASTM C210
	0.20 % @Temperature 1260 °C	0.20 % @Temperature 2300 °F	Permanent Linear Change; ASTM C210
	0.80 - 2.8 % @Temperature 1371 °C	0.80 - 2.8 % @Temperature 2500 °F	Permanent Linear Change