- BASF Ultradur B 4300 G2 BK5110 10% Glass Filled PBT
BASF Ultradur B 4300 G2 BK5110 10% Glass Filled PBT
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 10% Glass Fiber Filled |
| Manufacturer | BASF |
| Trade Name | Ultradur B |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | BASF Ultradur B 4300 G2 BK5110 10% Glass Filled PBT.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Ultradur B 4300 G2 BK5110 is a pigmented black, easy flowing injection molding PBT with 10% glass fiber reinforcement for rigid, tough, and dimensionally stable parts.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 |
| Water Absorption | 0.20 % | 0.20 % | 24 hour; ISO Test |
| 0.40 % | 0.40 % | ISO 62 | |
| Moisture Absorption at Equilibrium | 0.20 % | 0.20 % | 23°C/50% R.H.; ISO 62 |
| Viscosity Test | 116 cm³/g | 116 cm³/g | Viscosity number |
| Linear Mold Shrinkage | 0.0080 cm/cm | 0.0080 in/in | ASTM Data; MD |
| Melt Flow | 16 g/10 min @Load 2.16 kg, Temperature 250 °C |
16 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Ultimate | 85.0 MPa | 12300 psi | 5mm/min; ISO 527 |
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527 |
| Tensile Modulus | 4.20 GPa | 609 ksi | 1mm/min; ISO 527 |
| Flexural Modulus | 4.20 GPa | 609 ksi | ISO Data |
| Izod Impact, Notched (ISO) | 4.70 kJ/m² | 2.24 ft-lb/in² | ISO Test |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Melting Point | 223 °C | 433 °F | 10 K/min |
| 223 °C | 433 °F | ASTM Test | |
| Deflection Temperature at 1.8 MPa (264 psi) | 185 °C | 365 °F | ISO 75 |
| Flammability, UL94 | HB @Thickness 1.55 mm |
HB @Thickness 0.0610 in |
|
| HB @Thickness 0.400 mm |
HB @Thickness 0.0157 in |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Color | BK5110 | |
| Commercial Status | North America and Europe | |
| Form | Pellets | |
| Impact Modified | No | |
| Primary Processing Technique | Injection Molding | |
| Special characteristic | Heat stabilized or stable to heat | |
| Light stabilized or stable to light | ||
| Lubricant | ||
| U.V. stabilized or stable to weather |
Users viewing this material also viewed the following:
- Multibase Multi-Flex® TPO D-6510
- SABIC Innovative Plastics Lexan® FXG141R PC (Europe-Africa-Middle East)
- Americas Styrenics Styron® 484C High Impact Polystyrene (discontinued **)
- Kolon KOPA® KN333G15 G/F Reinforced Nylon 66
- Fainplast Compounds RKS 321 Rigid PVC, Antishock Extrusion Lead Free
- Sekisui PIOCELAN OP-E30ENS (Antistatic) Moldable Polymer Foam
- Polyplastics FR-PET® CN9030 Glass Fiber Reinforced Polyethylene Terephthalate (GF-PET), Flame retardant, General purpose
- American Polymers API 550 HF Polystyrene
- Dow DOWLEX™ 2045A Linear Low Density Polyethylene, Blown Film Grade
- Azoty Tarnow™ TARNOFORM 300 LS POM
Copyright © lookpolymers.com All Rights Reserved