BASF Petra® 110 BK-112 15% Glass Filled PET

Category	Polymer , Thermoplastic , Polyester, TP , Polyethylene Terephthalate (PET) , Polyethylene Terephthalate (PET), 20% Glass Reinforced
Manufacturer	BASF
Trade Name	Petra®
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	BASF Petra® 110 BK-112 15% Glass Filled PET.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Petra 110 is a 15% glass fiber reinforced, black pigmented, polyethylene terephthalate injection molding compound. It exhibits a good combination of performance properties including good strength and stiffness at elevated temperatures with good chemical resistance and dimensional stability.

Physical Properties	Metric	English	Comments
Density	1.44 g/cc	0.0520 lb/in³	ISO 1183
Linear Mold Shrinkage	0.0050 cm/cm	0.0050 in/in	ASTM Data; MD

Mechanical Properties	Metric	English	Comments
Tensile Strength at Break	105 MPa	15200 psi	0.2 in/min; ASTM Test
Tensile Strength, Ultimate	105 MPa	15200 psi	5mm/min; ISO 527
Elongation at Break	3.5 %	3.5 %	5mm/min; ISO 527
	3.5 %	3.5 %	0.2 in/min; ASTM Test
Tensile Modulus	6.68 GPa	969 ksi	1mm/min; ISO 527
Flexural Strength	145 MPa	21000 psi	ASTM Test
Flexural Modulus	5.35 GPa	776 ksi	ASTM Test
	5.48 GPa	795 ksi	ISO Data
Izod Impact, Notched	0.650 J/cm @Thickness 3.17 mm	1.22 ft-lb/in @Thickness 0.125 in	ASTM Test
Izod Impact, Notched (ISO)	6.00 kJ/m²	2.86 ft-lb/in²	ISO Test
Charpy Impact, Notched	0.600 J/cm²	2.86 ft-lb/in²	ISO 179

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	32.0 µm/m-°C	17.8 µin/in-°F	ISO 11359
CTE, linear, Transverse to Flow	79.0 µm/m-°C	43.9 µin/in-°F	ISO 11359
Melting Point	245 °C	473 °F	10 K/min
	245 °C	473 °F	ASTM Test
Deflection Temperature at 0.46 MPa (66 psi)	231 °C	448 °F	ISO 75
Deflection Temperature at 1.8 MPa (264 psi)	192 °C	378 °F	ISO 75
	208 °C	406 °F	ASTM Test
Flammability, UL94	HB @Thickness 0.810 mm	HB @Thickness 0.0319 in
	HB @Thickness 3.00 mm	HB @Thickness 0.118 in

Electrical Properties	Metric	English	Comments
Dielectric Constant	3.3 @Frequency 1.00e+6 Hz	3.3 @Frequency 1.00e+6 Hz	IEC 60250
	3.4 @Frequency 100 Hz	3.4 @Frequency 100 Hz	IEC 60250
Dielectric Strength	36.0 kV/mm	914 kV/in	IEC 60243-1
Dissipation Factor	0.010 @Frequency 100 Hz	0.010 @Frequency 100 Hz	IEC 60250
	0.020 @Frequency 1.00e+6 Hz	0.020 @Frequency 1.00e+6 Hz	IEC 60250

Processing Properties	Metric	English	Comments
Melt Temperature	275 °C	527 °F	Injection molding
Mold Temperature	115 °C	239 °F	Injection molding

Descriptive Properties	Value	Comments
Color	BK-112
Commercial Status	Active America
Form	Pellets
Impact Modified	No
Primary Processing Technique	Injection Molding
Processing	Injection Molding
UL.UL-C	Yes