- Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant
- Ashley Polymers Ashlene® F242 ABS
Ashley Polymers Ashlene® F242 ABS
| Category | Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Unreinforced, Flame Retardant |
| Manufacturer | Ashley Polymers |
| Trade Name | Ashlene® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Ashley Polymers Ashlene® F242 ABS.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Flame retardant.Data provided by the manufacturer
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | Typical value for ABS |
| Melt Flow | 3.2 g/10 min | 3.2 g/10 min |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 104 | 104 | ASTM D785 |
| Tensile Strength, Ultimate | 45.0 MPa | 6530 psi | ATSM D638 |
| Flexural Strength | 70.0 MPa | 10200 psi | ASTM D790 |
| Flexural Modulus | 2.50 GPa | 363 ksi | ASTM D790 |
| Izod Impact, Notched | 1.55 J/cm | 2.90 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 78.0 °C | 172 °F | ASTM D648 |
| Flammability, UL94 | V-0 @Thickness 1.60 mm |
V-0 @Thickness 0.0630 in |
Users viewing this material also viewed the following:
- Nyco NYAD® M200 Wollastonite
- PTS PBT-1100 PBT Resin
- 3M Dyneon™ Fluorel™ FC-2110Q Fluoroelastomer VF2 + HFP Dipolymer (discontinued **)
- MV Labs ZN500 ZnF2 Zinc fluoride
- Polykemi AB POLYshine PBT D204 GF30 FR PBT, Glass Fiber Reinforced, Flame Retardant
- Eastman 5284 LDPE 8% EVA Copolymer, High Clarity, Ultra-High Impact Film Resin (discontinued **)
- ITW Plexus Plexusâ„¢ MA330 Methacrylate Adhesive
- Solvay Specialty Polymers Solef® 1015 Polyvinylidene Fluoride (PVDF)
- Solvay ALKAQUAT® DMB-451 80% Surfactant
- A. Schulman POLYBATCH™ Green 3251V Concentrate Based In Polyethylene
Copyright © lookpolymers.com All Rights Reserved