Asahi Kasei Thermylene® P-10TC-1777 10% Talc Filled, UV Stabilized Polypropylene
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 10% Talc Filler |
| Manufacturer | Asahi Kasei |
| Trade Name | Thermylene® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Asahi Kasei Thermylene® P-10TC-1777 10% Talc Filled, UV Stabilized Polypropylene.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Asahi Thermofil
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 0.970 g/cc | 0.970 g/cc | ASTM D792 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 24.1 MPa | 3500 psi | ASTM D638 |
| Flexural Strength | 32.4 MPa | 4700 psi | ASTM D790 |
| Flexural Modulus | 1.24 GPa | 180 ksi | ASTM D790 |
| Izod Impact, Notched | 13.3 J/cm | 25.0 ft-lb/in | ASTM D256 |
Users viewing this material also viewed the following:
- Nye Lubricants 782LC (NG) Synthetic Oil
- Sekisui PIOCELAN OP-15E Moldable Polymer Foam
- SGL Carbon Group PANOX® FM C063 EEA Oxidized Textile Fiber, Crimped staple fiber, For carbon/carbon and spinning
- Techmer ES Electrablend® PA6/6 C14 BK 14% Carbon Filled
- SABIC Innovative Plastics LNP THERMOCOMP LF006 PEEK (Europe-Africa-Middle East)
- Supreme Petrochem SP 6425 9885 Abrasion Resistant Polystyrene
- Hexcel® HexForce™ KA060 Aramid and High Performance Fabrics
- 3M Scotchlite™ 680-10 Reflective Graphic Film
- 3M 5300 Motor Lead Splicing Kits
- Formosa Plastics Formolene® LH5204 Injection Molding HDPE (discontinued **)
Copyright © lookpolymers.com All Rights Reserved