- Arkema Group Pebax® 3533 Polyether Block Amide (PEBA)
Arkema Group Pebax® 3533 Polyether Block Amide (PEBA)
| Category | Polymer , Thermoplastic , Elastomer, TPE , Polyether Block Amide (PEBA) |
| Manufacturer | Arkema |
| Trade Name | Pebax® |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Arkema Group Pebax® 3533 Polyether Block Amide (PEBA).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Arkema Group
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 24 hr in water at 20°C; ASTM D570 |
| Water Absorption at Saturation | 0.50 % | 0.50 % | 20°C and 65% RH; ASTM D570 |
| Melt Flow | 8.0 g/10 min | 8.0 g/10 min | ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 83 | 83 | ASTM D2240 |
| Hardness, Shore D | 33 | 33 | ASTM D2240 |
| Tensile Strength at Break | 30.0 MPa | 4350 psi | ASTM D638 |
| Elongation at Break | 670 % | 670 % | ASTM D638 |
| Modulus of Elasticity | 0.0146 GPa | 2.12 ksi | ASTM D638 |
| Flexural Modulus | 0.0250 GPa | 3.63 ksi | ASTM D790 |
| Resilience | 0.70 | 0.70 | BS 903 par: A 8 |
| Flex Crack Resistance | 2.0 | 2.0 | [mm] 20°C / 100000 flexures; ASTM D813 |
| 2.5 | 2.5 | [mm] -20°C / 50000 flexures; ASTM D813 | |
| Izod Impact, Notched | NB | NB | ASTM D256-A |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256-A | |
| Izod Impact, Unnotched | NB | NB | ASTM D256-A |
| NB @Temperature -40.0 °C |
NB @Temperature -40.0 °F |
ASTM D256-A | |
| Tear Strength | 45.0 kN/m | 257 pli | notched; ASTM D624 (C) |
| 71.0 kN/m | 405 pli | unnotched; ASTM D624 (C) | |
| Taber Abrasion, mg/1000 Cycles | 81 | 81 | ASTM D1242 |
| Abrasion | 96 | 96 | mm<sup>3</sup>; DIN 53516 |
| Compression Set | 54 % | 54 % | Load = 9.3 MPa (22 hr / 70°C); ASTM D395 Method A |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Heat of Fusion | 11.0 J/g | 4.73 BTU/lb | ASTM D3417 |
| CTE, linear | 210 µm/m-°C @Temperature -40.0 - 140 °C |
117 µin/in-°F @Temperature -40.0 - 284 °F |
ASTM D696 |
| Melting Point | 143.5 °C | 290.3 °F | ASTM D3418 |
| Deflection Temperature at 0.46 MPa (66 psi) | 46.0 °C | 115 °F | ASTM D648 |
| Vicat Softening Point | 74.0 °C | 165 °F | under 1 daN; ASTM D1525 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Surface Resistance | 2.00e+12 ohm @Temperature 20.0 °C |
2.00e+12 ohm @Temperature 68.0 °F |
65% RH; ASTM D257 |
Users viewing this material also viewed the following:
- LG Chemical LUCEL N115-LD Anti Mold Deposit POM, Unreinforced, Internally Lubricated, Standard Viscosity
- SABIC Innovative Plastics LNP STAT-KON DE004ER PC
- Von Roll Isola IMI Varnish 74011 Solventless Epoxy Varnish for Electrical Insulation
- A. Schulman POLYFORT™ FXP 2600-3120 CaC02 Filled Homopolymer Polypropylene
- Eastman Tenite Butyrate 565A2R30016 Natural, Trsp Cellulose Acetate Butyrate
- ExxonMobil HD Plus 85W-140
- Chicago Extruded Metals UNS C36010 Copper-Zinc-Lead Alloy
- Colorite Polymers 7444D General Purpose Vinyl Compound
- Arlon TC350 Glass, PTFE and Micro-Dispersed Ceramic
Copyright © lookpolymers.com All Rights Reserved