Category | Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE |
Manufacturer | AlphaGary |
Trade Name | Evoprene™ HP |
Port | Shanghai port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | AlphaGary Evoprene™ HP 3730 High Performance Thermoplastic Elastomer.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 0.980 g/cc | 0.980 g/cc | ISO 2782 |
Viscosity Measurement | 16 @Temperature 150 °C |
16 @Temperature 302 °F |
Kg/cm<sup>2</sup>; Macklow-Smith extrusion rheometer |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 80 | 80 | ISO 868 |
Tensile Strength | 17.8 MPa | 2580 psi | ISO 37 |
Elongation at Break | 765 % | 765 % | ISO 37 |
100% Modulus | 0.00380 GPa | 0.551 ksi | ISO 37 |
200% Modulus | 0.00440 GPa | 0.638 ksi | ISO 37 |
300% Modulus | 0.00530 GPa | 0.769 ksi | ISO 37 |
Tear Strength | 61.0 kN/m | 348 pli | ISO 34-B |
Abrasion | 94 | 94 | mm<sup>3</sup>; DIN 53516 |
Compression Set | 36 % @Temperature 22.0 °C, Time 259000 sec |
36 % @Temperature 71.6 °F, Time 72.0 hour |
ISO 815 |
46 % @Temperature 70.0 °C, Time 79200 sec |
46 % @Temperature 158 °F, Time 22.0 hour |
ISO 815 | |
62 % @Temperature 100 °C, Time 79200 sec |
62 % @Temperature 212 °F, Time 22.0 hour |
ISO 815 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Maximum Service Temperature, Air | 125 °C | 257 °F | |
Minimum Service Temperature, Air | -60.0 °C | -76.0 °F |
Descriptive Properties | Value | Comments |
---|---|---|
Bonds with | Polypropylene | |
Chemical Resistance | Acetone | Moderate/Good |
Acids up to 80% | Excellent | |
Alcohol | Excellent | |
Alkalis | Excellent | |
Brake fluid | Good | |
Chlorinate solvents | Poor | |
Diesel | Poor | |
Ethylene glycol | Excellent | |
Gasoline | Poor | |
Salt solution | Excellent | |
Soda lye | Excellent | |
Water, 23°C | Excellent | |
Water, 95°C | Good |