Category | Polymer , Thermoplastic , Elastomer, TPE , Styrenic TPE |
Manufacturer | AlphaGary |
Trade Name | Evoprene™ G |
Port | Ningbo port,China |
Trade Terms | FOB, CFR, CIF |
Payment Terms | L/C, T/T, Western Union |
Download PDF | AlphaGary Evoprene™ G 992 SEBS Thermoplastic Elastomer.pdf |
Price | EMAIL US sales@lookpolymers.com |
Physical Properties | Metric | English | Comments |
---|---|---|---|
Specific Gravity | 1.20 g/cc | 1.20 g/cc | ISO 2782 |
Viscosity Measurement | 16 @Temperature 180 °C |
16 @Temperature 356 °F |
Kg/cm<sup>2</sup>; Macklow-Smith extrusion rheometer |
Mechanical Properties | Metric | English | Comments |
---|---|---|---|
Hardness, Shore A | 43 | 43 | ISO 868 |
Tensile Strength | 5.00 MPa | 725 psi | ISO 37 |
Elongation at Break | 605 % | 605 % | ISO 37 |
100% Modulus | 0.00100 GPa | 0.145 ksi | ISO 37 |
Tear Strength | 20.0 kN/m | 114 pli | ISO 34-B |
Compression Set | 27 % @Temperature 22.0 °C, Time 259000 sec |
27 % @Temperature 71.6 °F, Time 72.0 hour |
ISO 815 |
36 % @Temperature 70.0 °C, Time 79200 sec |
36 % @Temperature 158 °F, Time 22.0 hour |
ISO 815 | |
61 % @Temperature 100 °C, Time 79200 sec |
61 % @Temperature 212 °F, Time 22.0 hour |
ISO 815 |
Thermal Properties | Metric | English | Comments |
---|---|---|---|
Maximum Service Temperature, Air | 110 - 120 °C | 230 - 248 °F | |
Minimum Service Temperature, Air | -60.0 - -40.0 °C | -76.0 - -40.0 °F |
Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | |
Dielectric Strength | 24.0 - 28.0 kV/mm | 610 - 711 kV/in |
Descriptive Properties | Value | Comments |
---|---|---|
Bonds with | Polypropylene | |
Chemical Resistance | Acetone | Moderate/Good |
Acids up to 80% | Excellent | |
Alcohol | Excellent | |
Alkalis | Excellent | |
Brake fluid | Good | |
Chlorinate solvents | Poor | |
Diesel | Poor | |
Ethylene glycol | Excellent | |
Gasoline | Poor | |
Salt solution | Excellent | |
Soda lye | Excellent | |
Water, 23°C | Excellent | |
Water, 95°C | Good | |
Transparency | Opaque |