Adamas Adalon® 103 PTFE, 10% Carbon Filled
| Category | Polymer , Thermoplastic , Fluoropolymer , PTFE , Polytetrafluoroethylene (PTFE), Carbon Fiber Filled |
| Manufacturer | Adamas |
| Trade Name | Adalon® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Adamas Adalon® 103 PTFE, 10% Carbon Filled.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information provided by Adamas, HPM
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 2.15 - 2.16 g/cc | 2.15 - 2.16 g/cc | ASTM D792 |
| Deformation | 2.0 - 4.8 % | 2.0 - 4.8 % | Permanent deformation after 24 hrs @ 23°C; ASTM D621 |
| 8.9 - 10.6 % | 8.9 - 10.6 % | ASTM D621 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 62 - 64 | 62 - 64 | ASTM D2240 |
| Tensile Strength at Break | >= 20.0 MPa | >= 2900 psi | ASTM D4894 |
| Elongation at Break | >= 200 % | >= 200 % | ASTM D4894 |
| Compressive Strength | >= 10.0 MPa @Temperature 23.0 °C, Time 86400 sec |
>= 1450 psi @Temperature 73.4 °F, Time 24.0 hour |
@ 1% deformation, 140 Kg/cm<sup>2</sup>; ASTM D621 |
| Coefficient of Friction, Dynamic | 0.10 - 0.11 | 0.10 - 0.11 | ASTM D1894 |
| Coefficient of Friction, Static | 0.14 - 0.16 | 0.14 - 0.16 | ASTM D1894 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Thermal Conductivity | 0.260 W/m-K | 1.80 BTU-in/hr-ft²-°F | ASTM C 177 |
| Melting Point | 327 °C | 621 °F | DSC |
| Maximum Service Temperature, Air | 260 °C | 500 °F | DSC |
| Minimum Service Temperature, Air | -80.0 °C | -112 °F | DSC |
| Flammability, UL94 | V-0 | V-0 |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+7 ohm-cm | 1.00e+7 ohm-cm | ASTM D257 |
| Surface Resistance | 1.00e+6 ohm | 1.00e+6 ohm | ASTM D257 |
Users viewing this material also viewed the following:
- MV Labs BA400 BaCl2 Barium chloride
- MV Labs PT487 Pt(C2H8N2)2Cl2 Bis(ethylenediamine)platinum(II) chloride
- Kennametal Stellite Stellite® 98M2 cast
- Glastic Laminates/Shapes 1603-2A Fiberglass-Reinforced Polyester Standoff Insulator
- H.C. Starck Molybdenum Alloy AFB-3OW, Arc-Cast Forging Billet
- Saint-Gobain Chemfab® 250GW PTFE Coated Beta Fiberglass with Woven-in Graphite Conveyor Belting
- EDRO EDRO400™ #40 Prehardened Insert Quality Martensitic Stainless Steel
- EMS-Grivory Grivory® GVL-5H nat PA*-GF50
- TSE Industries Millathane® 76 Millable Polyester Polyurethane Rubber, Hardness 60A, Black Sulfur Cure
Copyright © lookpolymers.com All Rights Reserved