Aclo Accutech Polypropylene Copolymer CP0436C30L Calcium Reinforced
| Category | Polymer , Thermoplastic , Polypropylene (PP) , Polypropylene with 30% Calcium Carbonate (CaCO3) Filler |
| Manufacturer | Aclo Compounders |
| Trade Name | Accutech |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Aclo Accutech Polypropylene Copolymer CP0436C30L Calcium Reinforced.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.11 g/cc | 0.0401 lb/in³ | ASTM D792 |
| Linear Mold Shrinkage | 0.010 cm/cm | 0.010 in/in | MD; ASTM D955 |
| Melt Flow | 10 g/10 min | 10 g/10 min | ASTM D1238 |
| Ash | 30 % | 30 % | ASTM D2584 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 58 | 58 | ASTM D785 |
| Tensile Strength at Break | 15.0 MPa | 2180 psi | ASTM D638 |
| Tensile Strength, Yield | 19.0 MPa | 2760 psi | ASTM D638 |
| Elongation at Break | 48 % | 48 % | ASTM D638 |
| Elongation at Yield | 3.0 % | 3.0 % | ASTM D638 |
| Tensile Modulus | 1.60 GPa | 232 ksi | ASTM D638 |
| Flexural Strength | 25.0 MPa | 3630 psi | ASTM D790 |
| Flexural Modulus | 1.40 GPa | 203 ksi | ASTM D790 |
| Izod Impact, Notched | 0.908 J/cm | 1.70 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 93.9 °C | 201 °F |
Users viewing this material also viewed the following:
- Radici Radilon® A RCV3015 RKC Nylon 66-GF30
- Global PP-3240-H Polypropylene Random Copolymer
- Kazanorgsintez Diproxamine 157
- Latrobe Lescalloy® 4340 VAC-ARC ; 10.5" square High Strength Alloy Steel
- SSAB Tunnplat Docol® 260 RP High-strength Steel
- SABIC Innovative Plastics LNP THERMOCOMP EC008 PEI (Europe-Africa-Middle East)
- Samsung Cheil Industries Infino® NH-1014S PC/ABS, Unreinforced FR
- A. Schulman POLYFORT™ FPP 1310 Coupled Mica Filled Homopolymer Polypropylene
- Akzo Nobel Expancel® 820 SL 40 Unexpanded microspheres in aqueous dispersion
- Arlon R35928R015 0.0155" (0.394 mm) Uncured/Cured Silicone Rubber with Fiberglass Substrate
Copyright © lookpolymers.com All Rights Reserved