3M Fastbond™ 30H-NF Contact Adhesive

Category Polymer , Adhesive
Manufacturer 3M
Trade Name Fastbond™
Port Shanghai port,China
Trade Terms EXW, FOB, CFR, CIF
Payment Terms L/C, T/T, PayPal
Download PDF 3M Fastbond™ 30H-NF Contact Adhesive.pdf
Price EMAIL US    sales@lookpolymers.com
Material Notes:
3M Fastbond™ Contact Adhesive 30-NF and 30H-NF are water-dispersed, sprayable contact adhesives for high immediate bond strength n long bonding range.Information provided by 3M
Physical Properties Metric English Comments
Solids Content 45 - 50 %
45 - 50 %
Brookfield Viscosity 5500 - 9500 cP
5500 - 9500 cP
RVF #4 sp @ 20 rpm @ 77°F
Mechanical Properties Metric English Comments
Tensile Strength at Break 0.186 MPa
<br>@Temperature 93.0 °C
 27.0 psi
<br>@Temperature 199 °F
 Flatwise, high pressure laminate/particle board, test speed 0.05 in/min
0.207 MPa
<br>@Temperature 82.0 °C
 30.0 psi
<br>@Temperature 180 °F
 Flatwise, high pressure laminate/particle board, test speed 0.05 in/min
0.379 MPa
<br>@Temperature 66.0 °C
 55.0 psi
<br>@Temperature 151 °F
 Flatwise, high pressure laminate/particle board, test speed 0.05 in/min
0.779 MPa
<br>@Temperature 24.0 °C
 113 psi
<br>@Temperature 75.2 °F
 Flatwise, high pressure laminate/particle board, test speed 0.05 in/min
Shear Strength 0.207 MPa
<br>@Temperature 93.0 °C
 30.0 psi
<br>@Temperature 199 °F
 Overlap, 1/8&quot; birch 1/8&quot; birch
0.207 MPa
<br>@Temperature 82.0 °C
 30.0 psi
<br>@Temperature 180 °F
 1/8&quot; Birch/High-Pressure Laminate, no aging
0.276 MPa
<br>@Temperature 102 °C
 40.0 psi
<br>@Temperature 216 °F
 Overlap, 1/8&quot; birch 1/8&quot; birch
0.345 MPa
<br>@Temperature 82.0 °C
 50.0 psi
<br>@Temperature 180 °F
 1/8&quot; Birch/High-Pressure Laminate, aged 9 mo
0.414 MPa
<br>@Temperature 82.0 °C
 60.0 psi
<br>@Temperature 180 °F
 Overlap, 1/8&quot; birch 1/8&quot; birch
0.517 MPa
<br>@Temperature 82.0 °C
 75.0 psi
<br>@Temperature 180 °F
 1/8&quot; Birch/High-Pressure Laminate, aged 6 mo
0.552 MPa
<br>@Temperature 82.0 °C
 80.0 psi
<br>@Temperature 180 °F
 1/8&quot; Birch/High-Pressure Laminate, aged 3 mo
0.862 MPa
<br>@Temperature 66.0 °C
 125 psi
<br>@Temperature 151 °F
 1/8&quot; Birch/High-Pressure Laminate, aged 9 mo
0.896 MPa
<br>@Temperature 66.0 °C
 130 psi
<br>@Temperature 151 °F
 1/8&quot; Birch/High-Pressure Laminate, no aging
0.965 MPa
<br>@Temperature 66.0 °C
 140 psi
<br>@Temperature 151 °F
 1/8&quot; Birch/High-Pressure Laminate, aged 3 mo
1.03 MPa
<br>@Temperature 66.0 °C
 150 psi
<br>@Temperature 151 °F
 1/8&quot; Birch/High-Pressure Laminate, aged 6 mo
1.83 MPa
<br>@Temperature 24.0 °C
 265 psi
<br>@Temperature 75.2 °F
 1/8&quot; Birch/High-Pressure Laminate, no aging
1.97 MPa
<br>@Temperature 24.0 °C
 285 psi
<br>@Temperature 75.2 °F
 1/8&quot; Birch/High-Pressure Laminate, aged 9 mo
2.10 MPa
<br>@Temperature 24.0 °C
 305 psi
<br>@Temperature 75.2 °F
 1/8&quot; Birch/High-Pressure Laminate, aged 6 mo
2.17 MPa
<br>@Temperature 24.0 °C
 315 psi
<br>@Temperature 75.2 °F
 1/8&quot; Birch/High-Pressure Laminate, aged 3 mo
3.31 MPa
<br>@Temperature 24.0 °C
 480 psi
<br>@Temperature 75.2 °F
 Overlap, 1/8&quot; birch 1/8&quot; birch
7.58 MPa
<br>@Temperature -37.0 °C
 1100 psi
<br>@Temperature -34.6 °F
 Overlap, 1/8&quot; birch 1/8&quot; birch
Peel Strength 0.877 kN/m
<br>@Temperature -37.0 °C,<br> Time 1.81e+6 sec
 5.00 pli
<br>@Temperature -34.6 °F,<br> Time 504 hour
 canvas/canvas
1.75 kN/m
<br>@Temperature 66.0 °C,<br> Time 1.81e+6 sec
 10.0 pli
<br>@Temperature 151 °F,<br> Time 504 hour
 canvas/canvas
1.75 kN/m
<br>@Temperature 82.0 °C,<br> Time 1.81e+6 sec
 10.0 pli
<br>@Temperature 180 °F,<br> Time 504 hour
 canvas/canvas
2.63 kN/m
<br>@Temperature 24.0 °C,<br> Time 1.81e+6 sec
 15.0 pli
<br>@Temperature 75.2 °F,<br> Time 504 hour
 canvas/canvas
3.51 kN/m
<br>@Temperature 24.0 °C,<br> Time 605000 sec
 20.0 pli
<br>@Temperature 75.2 °F,<br> Time 168 hour
 canvas/canvas
3.51 kN/m
<br>@Temperature 24.0 °C,<br> Time 1.21e+6 sec
 20.0 pli
<br>@Temperature 75.2 °F,<br> Time 336 hour
 canvas/canvas
4.38 kN/m
<br>@Temperature 24.0 °C,<br> Time 86400 sec
 25.0 pli
<br>@Temperature 75.2 °F,<br> Time 24.0 hour
 canvas/canvas
5.26 kN/m
<br>@Temperature 24.0 °C,<br> Time 432000 sec
 30.0 pli
<br>@Temperature 75.2 °F,<br> Time 120 hour
 canvas/canvas
6.14 kN/m
<br>@Temperature 24.0 °C,<br> Time 259000 sec
 35.0 pli
<br>@Temperature 75.2 °F,<br> Time 72.0 hour
 canvas/canvas
Descriptive Properties Value Comments
Appearance Blue (Wet), Green (Dry)
Base Polychloroprene