3M Dyneon™ FE 5840Q Fluoroelastomer

Category	Polymer , Thermoset , Fluoropolymer, TS , Rubber or Thermoset Elastomer (TSE)
Manufacturer	3M Dyneon™
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	3M Dyneon™ FE 5840Q Fluoroelastomer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Composition: Terpolymer of vinylidene fluoride, hexafluoropropylene and tetrafluoroethyleneRecommended alternative for Dyneon FX 9038Process targets: compression, injection and transfer moldingProprietary incorporated cure technologyHigh fluorine material designed for O-ring and gasket applicationsRecommended for automotive fuel system applicationsClean runningExcellent mold releaseInformation provided by Dyneon, A 3M Company

Physical Properties	Metric	English	Comments
Specific Gravity	1.89 g/cc	1.89 g/cc
Mooney Viscosity	37 @Temperature 121 °C	37 @Temperature 250 °F	ML1+10

Mechanical Properties	Metric	English	Comments
Hardness, Shore A	84	84	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C; ASTM D2240
Tensile Strength at Break	13.8 MPa	2000 psi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
Elongation at Break	210 %	210 %	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
100% Modulus	0.00676 GPa	0.980 ksi	Press Cure 5 minutes @ 177°C, Post Cure 24 hours @ 260°C
Compression Set	26 %	26 %	Aged 70 hours @ 200°C

Thermal Properties	Metric	English	Comments
Transformation Temperature	-7.00 °C	19.4 °F	TR10; ASTM D1329

Component Elements Properties	Metric	English	Comments
Fluorine, F	70.1 %	70.1 %

Descriptive Properties	Value	Comments
Color	Opaque Off-White
MH, Maximum Torque	24 inch-lb	100 cpm, 0.5° Arc, 6 Minutes @ 200°C
	25.5 inch-lb	100 cpm, 0.5° Arc, 6 Minutes @ 177°C
ML, Minimum Torque	1.7 inch-lb	100 cpm, 0.5° Arc, 6 Minutes @ 177°C
	1.7 inch-lb	100 cpm, 0.5° Arc, 6 Minutes @ 200°C
Solubility	Ketones and Esters
t`50, Time to 50% cure	0.5 minutes	100 cpm, 0.5° Arc, 6 Minutes @ 200°C
t`50, Time to 50% cure	1.6 minutes	100 cpm, 0.5° Arc, 6 Minutes @ 177°C
t`90 - Time to 90% cure	0.6 minutes	100 cpm, 0.5° Arc, 6 Minutes @ 200°C
	2 minutes	100 cpm, 0.5° Arc, 6 Minutes @ 177°C
ts2 - Time to 2 in-lb rise from min	0.4 minutes	100 cpm, 0.5° Arc, 6 Minutes @ 200°C
	1.3 minutes	100 cpm, 0.5° Arc, 6 Minutes @ 177°C