Electrical Properties | Metric | English | Comments |
---|---|---|---|
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IEC 60093 |
Raschig Group DECAL® 1760 Phenolic Glass-fiber reinforced phenolic molding compound. Very good electrical properties, good chemical resistance and mechanical properties. This product meets the allowed upper limits for heavy metals an.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IEC 60093 |
Raschig Group DECAL® 572R Phenolic Glass-fiber reinforced phenolic molding compound. Exceptional heat resistance with regard to maintaining surface finish and mechanical properties, outstanding mechanical properties, excellent rotati.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IEC 60093 |
Raschig Group DECAL® 666/8 Phenolic Glass-fiber reinforced phenolic molding compound with mineral fillers. High heat resistance, reduced mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This prod.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IEC 60093 |
Raschig Group DECAL® 666/8/2B Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meets the allowe.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IEC 60093 |
Raschig Group DECAL® 937 Phenolic Mica reinforced phenolic molding compound. This product meets the allowed upper limits for heavy metals and PCAs and also conforms to the requirements of the EU directives 2002/95 (RoHS), 2002/96 (W.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IEC 60093 |
Raschig Group MELOPLAS® 181.5 MF Cellulose-reinforced, phenol-modified MF molding compound (MPF) in white and colored shades. Very good electrical properties, high surface hardness, good mechanical strength, high UV and heat resis.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IEC 60093 |
Raschig Group RALUPOL® 2100 UP Polyester Organically and inorganically filled polyester molding compound. Low post-shrinkage, very good electrical values, good mechanical strength. This product meets the allowed upper limits for heavy meta.. |
|||
Volume Resistivity | 1.00e+6 - 1.00e+13 ohm-cm | 1.00e+6 - 1.00e+13 ohm-cm | ASTM D257 |
PolyOne Lubri-Tech™ AT-15MCF/15T Acetal-Copolymer, Carbon Fiber Reinforced, PTFE Lubricated
(discontinued **) Description/Features:Milled Carbon Fiber ReinforcedPTFE LubricatedUL 94 HBPolyOne First ChoiceInformation provided by PolyOne Corporation. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IEC 60093 |
Raschig Group RESINOL® 87120 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets .. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | ASTM D257 |
Toyobo T-661 Nylon 66, Standard Grade (Conditioned) Features: Non-reinforced, Standard GradeInformation provided by Toyobo. |
|||
Volume Resistivity | 1.00e+10 - 1.00e+13 ohm-cm | 1.00e+10 - 1.00e+13 ohm-cm | ASTM D257 |
Unitika UNILATE® 1 SC PET Antistatic gradeUNILATE® products are plate materials prepared by using a polyethylene terephthalate (PET resin) as the main component, blending it with glass staple fiber, inorganic filler, and ot.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | ASTM D257 |
Daelim H&L Plavis-G15 CM 15% Graphite Filled Aromatic Polyimide Bearing Compression Molded. Plavis-G-15: Graphite 15 wt% filled, Self lubricating grade for wear and friction applications.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | ASTM D257 |
Daelim H&L Plavis-G15 DF 15% Graphite Filled Aromatic Polyimide Bearing Direct Formed. Plavis-G-15: Graphite 15 wt% filled, Self lubricating grade for wear and friction applications.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded to 3 ca.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | ASTM D257 |
Daelim H&L Plavis-G15 ISO 15% Graphite Filled Aromatic Polyimide Bearing Isostatically Molded. Plavis-G-15: Graphite 15 wt% filled, Self lubricating grade for wear and friction applications.General Plavis information for all grades:PLAVIS polyimide has nitrogen bonded .. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IS 3396-1979 |
Amity Thermosets ATE 183 M Phenolic Molding Mica and organic Filler, Compression Molded Characteristics:Electric low loss Low water absorption Low shrinkage Heat stableGlossy surface finishVery good mouldabilityGood electrical insulationGood chemical resistantColor-blackMedium flowAppl.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IS 3396-1979 |
Amity Thermosets ATE 183 Phenolic Molding Mica and organic Filler, Compression Molded Characteristics:Electric low loss Low water absorption Low shrinkage Heat stableGlossy surface finishVery good mouldabilityGood electrical insulationGood chemical resistantColor-blackMedium flowAppl.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm @Temperature 100 °C |
1.00e+12 - 1.00e+13 ohm-cm @Temperature 212 °F |
|
China-Yixing Longly Refractories 75 Alumina Ceramic LONGLY selects high quality ceramic fine powder and micropowder as materials, adopts modern advanced molding technology to produce a multitude of ceramic tubes, rods, beads, balls, columns, plates, .. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IEC 60093 |
Raschig Group DECAL® 152CL Phenolic Glass-fiber and mineral reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and mechanical properties. This product meet.. |
|||
Volume Resistivity | 1.00e+12 - 1.00e+13 ohm-cm | 1.00e+12 - 1.00e+13 ohm-cm | IEC 60093 |
Raschig Group RESINOL® 400 EPF Phenolic Glass-fiber reinforced phenolic molding compound. Excellent heat resistance, low mould shrinkage and post-shrinkage, good chemical resistance and very good mechanical properties. This product meets .. |