Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Strength | 18.7 kV/mm | 475 kV/in | Short Term; ASTM D149 |
Quadrant EPP Semitron® ESd 520HR (ASTM Product Data Sheet) |
|||
Dielectric Strength | 18.7 kV/mm @Thickness 3.20 mm |
475 kV/in @Thickness 0.126 in |
in air; ASTM D149 |
SABIC Innovative Plastics Lexan® 3413R PC 30% GR, provides improved mechanical properties and UL94V-1 rated at 0.058"". Internal mold release added. |
|||
Dielectric Strength | 18.7 kV/mm @Thickness 3.20 mm |
475 kV/in @Thickness 0.126 in |
in air; ASTM D149 |
SABIC Innovative Plastics Lexan® 3413R PC (Asia Pacific) Lexan* resin 3413R is a flame retardant polycarbonate grade with 30% glass fiber reinforcement to meet UL 94 V1 listing at 1.5mm. This grade can be considered for applications requiring higher stiff.. |
|||
Dielectric Strength | 18.7 - 20.0 kV/mm | 475 - 508 kV/in | Average value: 19.6 kV/mm Grade Count:3 |
Overview of materials for Acrylic, Heat Resistant, Molded This property data is a summary of similar materials in the MatWeb database for the category "Acrylic, Heat Resistant, Molded". Each property range of values reported is minimum and maximum values o.. |
|||
Dielectric Strength | 18.7 kV/mm | 475 kV/in | |
Arkema Group Oroglas® MI-4T Acrylic, Heat Resistant
(discontinued **) OROGLAS MI-4T is an acrylic grade that associates improved impact resistance with high heat resistance.Key features improved impact resistance: up to 4 times more impact resistant than standard acr.. |
|||
Dielectric Strength | 18.7 kV/mm | 475 kV/in | |
XXX Phenolic Laminate Paper based phenolic provides low cost electrical and mechanical properties. It is widely used for switchboards, panel boards, insulating washers, and intricate punched parts.Information provided b.. |
|||
Dielectric Strength | 18.7 - 38.0 kV/mm | 475 - 965 kV/in | Average value: 25.5 kV/mm Grade Count:33 |
Overview of materials for Nylon 612, Glass Fiber Filler This property data is a summary of similar materials in the MatWeb database for the category "Nylon 612, Glass Fiber Filler". Each property range of values reported is minimum and maximum values of .. |
|||
Dielectric Strength | 18.7 kV/mm @Thickness 1.91 mm |
475 kV/in @Thickness 0.0750 in |
|
Momentive Performance Materials RTV8112 White General Purpose Potting/Encapsulating Compound Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate.. |
|||
Dielectric Strength | 18.7 kV/mm | 475 kV/in | ASTM D149 |
Plastics Group Polifil® 627L Nylon 6/6 (DAM) Polifil® NYLON 6/6 combines good abrasion and chemical resistance.Applications: ValvesBearingsBearing casesStandard processing techniques are applicable. Information provided by The Plastics Group... |
|||
Dielectric Strength | 18.7 kV/mm | 475 kV/in | |
Tokuyama Shapal™ SH-50 Sintered Aluminum Nitride Uniform, large sized pressed sintered aluminum nitride. |
|||
Dielectric Strength | 18.7 kV/mm | 475 kV/in | ASTM D149 |
Westlake Plastics Ultra Ethylux® HDPE Ultra Ethylux is made from high density polyethylene resin. This material is a cost effective alternative for a variety of end uses including mild chemical and wear applications. Information provid.. |
|||
Dielectric Strength | 18.7 kV/mm | 475 kV/in | ASTM D149 |
Arlon 56344R025 0.025" (0.635 mm) Semi-cured Silicone Rubber Design/Construction: Interleave: PolyethyleneSide 1: Semi-Cured Silicone Rubber Substrate: 1564 Style FiberglassAppearance: Red silicone gum on fiberglass clothThis data represents typical values fo.. |
|||
Dielectric Strength | 18.7 kV/mm | 475 kV/in | IEC 60243-1 |
DSM Arnitel® CM600-V TPC-ES FR Extrusion, Flame Retardant (Halogen free) |