Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Strength | 14.0 kV/mm | 356 kV/in | |
Plastcom SLOVAMID 6 GF 30 FRA 5 PA6, 30% glass fibre, flame retardant FeaturesPA 6 for injection moulding, chemically reinforced with 30% glass fibre, with halogen flame retardant. Main features: flammability in accordance with UL 94 V0 at 1.6 mm, glow wire at 960°C,.. |
|||
Dielectric Strength | 14.0 kV/mm @Thickness 3.20 mm |
356 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
SABIC Innovative Plastics EXTEM VH1003M PEI Copolymer Transparent, Thermoplastic Polyimide (TPI) resin with a glass transition temperature (Tg) of 247C. Internal mold release. This product has thinwall FR capability and has a UL94 V0 listing. This mate.. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | |
Pyrotek TS-83 Thermoset Electrical Insulation Product (Nema Grade: LE) Linen reinforcement, Phenolic resin, Tan / Black color. Good electrical and high mechanical strength. Moisture resistant.Information provided by Pyrotek. |
|||
Dielectric Strength | 14.0 - 35.0 kV/mm | 356 - 889 kV/in | Average value: 22.1 kV/mm Grade Count:49 |
Overview of materials for Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate/Polybutylene Terephthalate (PBT) Blend, Unreinforced". Each property range of values repor.. |
|||
Dielectric Strength | 14.0 kV/mm @Thickness 3.20 mm, Temperature 23.0 °C |
356 kV/in @Thickness 0.126 in, Temperature 73.4 °F |
ASTM D149 |
Solvay Specialty Polymers Halar® 500LC Polyethylene, Chlorotrifluoroethylene (ECTFE)
(Unverified Data**)& Information provided by Solvay Specialty Polymers. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | AC 60 Hz |
Fujipoly Industries Sarcon® 30GSR Thin-Film GSR Sarcon GSR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GSR is a composite of.. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | AC 60 Hz |
Fujipoly Industries Sarcon® 85H Thin-Film HR Sarcon HR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GHR is a composite of .. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | Perpendicular (ASTM D149), in Oil |
Haysite HCR-100 Corrosion Resistant Polyester/Glass Sheet A general purpose isophthalic polyester sheet with flame retardants and ultraviolet inhibitors. Standard color is gray. |
|||
Dielectric Strength | 14.0 - 26.0 kV/mm | 356 - 660 kV/in | DIN 53481 |
Isoflon PUR Polyurethane Very high wear resistanceHighly resilientInformation provided by Isoflon. |
|||
Dielectric Strength | 14.0 kV/mm @Thickness 3.18 mm |
356 kV/in @Thickness 0.125 in |
ASTM D149 |
Solvay Specialty Polymers Halar® 1400LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Low ViscosityUses: FibersAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 300 °CInformation provided by Solvay Spec.. |
|||
Dielectric Strength | 14.0 kV/mm @Thickness 3.18 mm |
356 kV/in @Thickness 0.125 in |
ASTM D149 |
Solvay Specialty Polymers Halar® 350LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 °CInformation provided by Solvay Specialty Pol.. |
|||
Dielectric Strength | 14.0 kV/mm @Thickness 3.18 mm |
356 kV/in @Thickness 0.125 in |
ASTM D149 |
Solvay Specialty Polymers Halar® 500LC Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Low ViscosityUses: Wire & Cable ApplicationsAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 °CInformation prov.. |
|||
Dielectric Strength | 14.0 kV/mm @Thickness 3.18 mm |
356 kV/in @Thickness 0.125 in |
ASTM D149 |
Solvay Specialty Polymers Halar® 930LCW Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) Medium ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 °CInformation provided by Solvay Specialty Pol.. |
|||
Dielectric Strength | 14.0 kV/mm @Thickness 3.20 mm |
356 kV/in @Thickness 0.126 in |
in oil; ASTM D149 |
SABIC Innovative Plastics ULTEM XH6050M PEI Copolymer Enhanced flow Polyetherimidesulfone copolymer (Tg 247C) with internal mold release. ECO Conforming, UL94 V0 listing. Resin is subject to U.S. Commerce Control Laws (15CFR Chapter VII, Part 774). |
|||
Dielectric Strength | 14.0 kV/mm @Thickness 3.18 mm |
356 kV/in @Thickness 0.125 in |
ASTM D149 |
Solvay Specialty Polymers Halar® 901 Ethylene Chlorotrifluoroethylene Copolymer (ECTFE) High ViscosityAdditional Properties: Crystallization Heat - ASTM D3418 40.0 J/g; Heat of Fusion - ASTM D3418 42.0 J/g; Thermal Stability - TGA 405 °CInformation provided by Solvay Specialty Polym.. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | GB/T1408.1-2006 |
Sichuan Deyang Haton® hMR60DL Polyphenylene Sulfide, Glass & Mineral Reinforced Injection molding, low chlorineInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | GB/T1408.1-2006 |
Sichuan Deyang Haton® hMR61LC1 Polyphenylene Sulfide, Glass & Mineral Reinforced Injection molding, high strengthInformation provided by Sichuan Deyang Chemical Co., LTD |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | ASTM D149-95a |
Thermoseal KLINGERSIL® C-4201 General Application Gasketing Synthetic FiberNitrile BinderExcellent Resistance to Oil & SolventsGood Anti-Stick PropertiesExcellent OEM MaterialInformation provided by Thermoseal Inc. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
Cosmic Plastics D72 Short Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
Cosmic Plastics D45 Mineral Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
Cosmic Plastics ID-40 Orlon Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | 2.8 kV minimum |
Arlon 0.008" (0.2032 mm) Primerless Thermabond® Uncured Silicone (99990A008) 0.008 in., ±0.001 (0.2 mm, ±0.03) uncured silicone on 0.003 in. (0.08 mm) nominal PTFE coated fiberglass; 0.001 in. (0.03 mm) FEP interleave; overall thickness 0.008 in ±0.001(0.2 mm ± 0.03). T.. |
|||
Dielectric Strength | 14.0 - 21.0 kV/mm | 356 - 533 kV/in | Average value: 16.5 kV/mm Grade Count:7 |
Overview of materials for Polyethylene Terephthalate (PET), Recycled, Glass Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polyethylene Terephthalate (PET), Recycled, Glass Reinforced". Each property range of values reported is.. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, step-by-step. ASTM D149 |
Sumitomo Bakelite North America FS-6 CAF Mineral Filled Diallyl Phthalate Isophthalate DAP Resin Isomer. Used for critical, high-performance military and commercial electrical components where long-term reliability is demanded.Meets the requirements of ASTM D5948 Type MI.. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | ST; ASTM D149 |
Sumitomo Bakelite North America RX® 853G Fiberglass Reinforced Phenolic Novolac RX 853G is a fiberglass reinforced phenolic novolac compound, featuring dimensional stability, moderate impact resistance, and good strength and modulus.Information supplied by Sumitomo Bak North Am.. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
Cosmic Plastics 3D36 Thermoset Polyester Molding Compound Data provided by the manufacturer. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | Wet, Step by Step |
Cosmic Plastics 6130 Long Glass Fiber Filled Ortho Diallyl Phthalate Molding Compound Data provided by the manufacturer. |
|||
Dielectric Strength | 14.0 kV/mm | 356 kV/in | ASTM D149 |
Chevron Phillips Ryton® R-4 04 PPS (Polyphenylene Sulfide)
(discontinued **) Ryton® PPS is used in many electronic and automotive applications because of its high strength, favorable electrical properties, and high temperature stability.Data provided by the manufacturer.Sol.. |