Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Strength | 6.50 kV/mm | 165 kV/in | AC 60 Hz |
Fujipoly Industries Sarcon® 20GTR Thin-Film GTR Sarcon TR is Fujipolys originally developed High Heat Conductive Silicone Rubber. Fine, high heat conductive ceramic particles are mixed with insulative silicone rubber.Sarcon GTR is a composite of .. |
|||
Dielectric Strength | 6.50 kV/mm | 165 kV/in | 60Hz, Step-by-Step, wet; ASTM D149 |
Sumitomo Bakelite North America SI 9002N-1 Silicone Compound Short fibergass reinforced silicone molding compound which offers moderate strength properties, dimensional stability, and excellent long-term thermal stability at elevated temperatures.Information .. |
|||
Dielectric Strength | 6.50 kV/mm | 165 kV/in | ASTM D149 |
Tipco Tipcolite® TEL 211 Phenolic Compound, Glass & Nylon Fibers, Soft Flow & Low Shrinkage Soft Flow Phenolic Compound, Reinforced with Glass & Nylon FibresApplications: Automotives & ElectricalProcessing: Compression & TransferInformation provided by the Manufacturer, Tipco Industries L.. |
|||
Dielectric Strength | 6.50 - 7.50 kV/mm @Temperature 90.0 °C |
165 - 191 kV/in @Temperature 194 °F |
IS 2584-1963 |
Amity Thermosets ATF 197 Phenolic Molding Inorganic and glass Filler, Compression Molded Characteristics:Flame retardantSpark resistant Good electrical insulationHeat stability ( 200°C )Good mouldability Low water absorptionLow shrinkageColor-blackSoft/medium flow Applications:Switchg.. |
|||
Dielectric Strength | 6.50 - 8.00 kV/mm @Temperature 90.0 °C |
165 - 203 kV/in @Temperature 194 °F |
IS 2584-1963 |
Amity Thermosets ATS 155 Phenolic Molding Inorganic and glass fiber Filler, Compression Molded Characteristics:Shock resistantElectrical low lossHigh mechanical strengthHeat stableHigh electrical insulationDimensional stabilityGood mechanical tension bearing strengthGood copper adhesion Color.. |
|||
Dielectric Strength | 6.50 kV/mm | 165 kV/in | 60Hz, Step-by-Step, wet; ASTM D149 |
Sumitomo Bakelite North America SI 9002J-1 Silicone Compound SI 9002J-1 is a short fiberglass reinforced silicone molding compound, which offers moderate strength properties, and dimensional stability and excellent long-term thermal stability at elevated temp.. |