Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, all-weld metal, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, mill annealed HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 1000 °C |
0.000116 ohm-cm @Temperature 1830 °F |
|
Haynes 75 Nickel Alloy Sheet, Annealed at 1925°F (1050°C) Haynes alloy 75 is a solution-strengthened nickel-chromium alloy with moderate strength to 1200°F (650°C). It is principally used in low stress elevated temperature applications requiring reas.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 25.4 mm thick bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 3.2 mm thick sheet, GTAW weld HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 30% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 50% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 50% cold rolled and 1 hour at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 50% cold rolled and 5000 hours at 500°C, air cooled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 6.4 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 9.5 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, all-weld metal, GMAW weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, plate and bar HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 1100 °C |
0.000116 ohm-cm @Temperature 2010 °F |
Temperature resistance factor (F) =1.071 |
Alloy Wire International RW 80 Ni-Cr Resistance Wire Used in heating elements and control resistors because of its electrical properties and resistance to oxidation under temperature cycling and frequent switching. Also used in hot cutting operations.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 0.71 mm thick sheet HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 10% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 19.1 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 31.8 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
Electrical Resistivity | 0.000116 ohm-cm @Temperature 24.0 °C |
0.000116 ohm-cm @Temperature 75.2 °F |
|
Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |