Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.000103 ohm-cm @Temperature 21.0 °C |
0.000103 ohm-cm @Temperature 69.8 °F |
|
H.C. Starck MP35N® Nickel/Cobalt/Chromium/Molybdenum Alloy MP35N is a nickel-cobalt based alloy of the Multiphase® alloy system that has ultra high strength, toughness, ductility, biocompatibility, and outstanding corrosion resistance. H.C. Starck offers.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 316°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.000103 ohm-cm @Temperature 500 °C |
0.000103 ohm-cm @Temperature 932 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |