- Polymer Property : Electrical Resistivity = 0.000123 ohm-cm
Polymer Property : Electrical Resistivity = 0.000123 ohm-cm Product List
Electrical PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 400 °C |
0.000123 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® G-30® alloy, all-weld metal, GTAW weld 3.2 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 400 °C |
0.000123 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® G-30® alloy, mill annealed HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, 0% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, 10% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, 40% cold worked sheet HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, SMAW weld, 316L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, GMAW short arc weldment, plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, GMAW spray weldment, 23.4 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys an.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 400 °C |
0.000123 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GMAW spray weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 400 °C |
0.000123 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® G-30® alloy, 6.4 mm thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxid.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 400 °C |
0.000123 ohm-cm @Temperature 752 °F |
|
| ATI Allegheny Ludlum Altemp® HX Nickel-Based superalloy Characteristics: outstanding resistance to oxidation at high temperatures, exceptional strength at elevated temperatures, good fabricability, good machinability in annealed condition, work hardening.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, all-weld metal, SMAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, as welded, notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, GTAW, as welded, unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, transverse, SMAW weldment, 19.1 mm thick plate HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 400 °C |
0.000123 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® G-30® alloy, 10% cold rolled HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 400 °C |
0.000123 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate, GTAW short arc weld 1.1 mm diameter filler wire HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, 0% cold worked sheet, aged 100 hours at 500°C HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, 6.4-19.1 mm thick plate, solution heat treated HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, all-weld metal, GTAW HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), notched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, GMAW, aged 4000 hours at 450°C (800°F), unnotched HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 100 °C |
0.000123 ohm-cm @Temperature 212 °F |
|
| Haynes Hastelloy® C-22® alloy, SMAW weld, 904L base metal, C-22 weld metal HASTELLOY® C-22® alloy is a nickel-chromium-molybdenum-tungsten alloy with excellent overall corrosion resistance compared to other Ni-Cr-Mo alloys, including HASTELLOY C-276 and C-4 alloys and al.. |
|||
| Electrical Resistivity | 0.000123 ohm-cm @Temperature 400 °C |
0.000123 ohm-cm @Temperature 752 °F |
|
| Haynes Hastelloy® G-30® alloy, 12.7 mm (1/2 in.) thick plate HASTELLOY® G-30® alloy is a high chromium nickel-base alloy which shows superior corrosion resistance in commercial phosphoric acids as well as many complex environments containing highly oxidizin.. |
|||