Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, 1.6 mm sheet Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, 12.7 mm (1/2 in.) thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, 12.7-50.8 mm bar Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, 19.1 mm thick plate, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, 6.3-38.1 mm plate Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 204°C (400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 316°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 427°C (800°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 538°C (1000°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 649°C (1200°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 760°C (1400°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 871°C (1600°F) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, aged 1000 hours at 982°C Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, all-weld metal, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, all-weld metal, GTAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, all-weld metal, SMAW weld Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, mill annealed Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (short) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 300 °C |
0.0000960 ohm-cm @Temperature 572 °F |
|
Haynes Ultimet® alloy, plate, GMAW weld (spray) Co content as balance, excellent corrosion resistance, outstanding wear resistance, high tensile strength combined with excellent impact toughness and ductility. Ideal welding material with exceptio.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 600 °C |
0.0000960 ohm-cm @Temperature 1110 °F |
|
Bohler-Uddeholm BÖHLER W302 SUPERIOR® Premium H13 Tool Steel A premium grade H13 hot work tool steel featuring:Very good toughness properties meeting the requirements of NADCA 207-97, and the superior quality levels of NADCA 207-2003Very good heat checking re.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 600 °C |
0.0000960 ohm-cm @Temperature 1110 °F |
|
Bohler-Uddeholm BÖHLER W400 VMR® H11 Hot Work Tool Steel W400 VMR is a low silicon, chromium-vanadium hot work tool steel which has been vacuum remelted to obtain the highest uniformity, the best cleanliness of tool steel. The material is characterized:E.. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 600 °C |
0.0000960 ohm-cm @Temperature 1110 °F |
|
Bohler-Uddeholm BÖHLER W403 VMR® Hot Work Tool Steel W403 VMR is a modified hot work alloy with an excellent combination of hot tensile properties and toughness. The balanced properties of this grade are not only due to chemistry modification, but to .. |
|||
Electrical Resistivity | 0.0000960 ohm-cm @Temperature 600 °C |
0.0000960 ohm-cm @Temperature 1110 °F |
|
Bohler-Uddeholm BÖHLER W302 ISOBLOC® H13 hot work tool steel Properties:Hot work tool steel featuring excellent hot tensile properties, high hot wear resistance, adequate toughness and heat checking resistance, adequate toughness and heat checking; admits wat.. |