Electrical Properties | Metric | English | Comments |
---|---|---|---|
Dielectric Breakdown | 5000 V @Thickness 1.57 mm |
5000 V @Thickness 0.0620 in |
D-48/50 |
Industrial Laminates/Norplex ES-1 Engraving Stock Description: Composed of white melamine paper core with various pigmented cover sheets.Thickness Tested: 0.0620â€, 0.125â€, and 0.500†|
|||
Dielectric Breakdown | 5000 V @Thickness 1.57 mm |
5000 V @Thickness 0.0620 in |
D-48/50 |
Industrial Laminates/Norplex ES-2 Engraving Stock Description: Composed of black phenolic paper core, sub surfaces of white melamine, and various pigmented cover plies. |
|||
Dielectric Breakdown | 5000 V @Thickness 1.57 mm |
5000 V @Thickness 0.0620 in |
D-48/50 |
Industrial Laminates/Norplex ES-3 Engraving Stock Description: Contains black phenolic/paper core and various colored covers impregnated with melamine resin. |
|||
Dielectric Breakdown | 5000 V @Thickness 1.57 mm |
5000 V @Thickness 0.0620 in |
Cond D-48/50; ASTM D229 S/S |
Industrial Laminates/Norplex NP322 Cotton Fabric Description: Linen phenolic laminate with molybdenum disulfide. Provides the same lubricity as NP313, but has better machining qualities. Mechanical strength similar to, but slightly less than NP320.. |
|||
Dielectric Breakdown | 5000 V @Thickness 1.57 mm |
5000 V @Thickness 0.0620 in |
Cond D-48/50; ASTM D229 S/S |
Industrial Laminates/Norplex NP329 Cotton Fabric Description: Bleached linen with melamine resin system. Provides better arc resistance than NP320E. Also, resistant to ammonia based refrigerants. Hard, durable material should be heated to punch, .. |
|||
Dielectric Breakdown | 5000 V @Thickness 1.57 mm |
5000 V @Thickness 0.0620 in |
Cond D-48/50; ASTM D229 S/S |
Industrial Laminates/Norplex NP629 Paper Base Laminate Description: It is a paper-phenolic high-pressure laminate. It is intended primarily for mechanical applications and is suitable for electrical applications as well. Thickness Tested: 0.062", 0.125".. |
|||
Dielectric Breakdown | 5000 V @Thickness 1.57 mm |
5000 V @Thickness 0.0620 in |
Cond D-48/50; ASTM D229 S/S |
Industrial Laminates/Norplex NP691 Paper Base Laminate Description: Flame resistant, room temperature punching grade. NP691 is very similar to NP612 in electrical properties and mechanical strength, with improved moisture resistance.Thickness Tested: 0... |
|||
Dielectric Breakdown | >= 5000 V @Temperature 90.0 °C, Time 20.0 sec |
>= 5000 V @Temperature 194 °F, Time 0.00556 hour |
Step -by-step test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CC 32 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. Coarse weave (18 to 30 threads per cm).Information provided by Hippe. |
|||
Dielectric Breakdown | >= 5000 V @Temperature 90.0 °C, Time 60.0 sec |
>= 5000 V @Temperature 194 °F, Time 0.0167 hour |
Proof test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CC 32 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. Coarse weave (18 to 30 threads per cm).Information provided by Hippe. |
|||
Dielectric Breakdown | >= 5000 V @Temperature 90.0 °C, Time 20.0 sec |
>= 5000 V @Temperature 194 °F, Time 0.00556 hour |
Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CC 33 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. Very coarse weave ( |
|||
Dielectric Breakdown | >= 5000 V @Temperature 90.0 °C, Time 60.0 sec |
>= 5000 V @Temperature 194 °F, Time 0.0167 hour |
Proof test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CC 33 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. Very coarse weave ( |
|||
Dielectric Breakdown | >= 5000 V @Temperature 90.0 °C, Time 20.0 sec |
>= 5000 V @Temperature 194 °F, Time 0.00556 hour |
Step -by-step test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CC 41 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical and electrical applications. Fine weave (more than 30 threads per cm).Information provided by Hippe. |
|||
Dielectric Breakdown | >= 5000 V @Temperature 90.0 °C, Time 60.0 sec |
>= 5000 V @Temperature 194 °F, Time 0.0167 hour |
Proof test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CC 41 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical and electrical applications. Fine weave (more than 30 threads per cm).Information provided by Hippe. |
|||
Dielectric Breakdown | >= 5000 V @Temperature 90.0 °C, Time 20.0 sec |
>= 5000 V @Temperature 194 °F, Time 0.00556 hour |
Step-by-step test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CC 31 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. Fine weave (>30 threads per cm).Information provided by Hippe. |
|||
Dielectric Breakdown | >= 5000 V @Temperature 90.0 °C, Time 60.0 sec |
>= 5000 V @Temperature 194 °F, Time 0.0167 hour |
Proof test, In oil, parallel to laminations; IEC 1212-2 5.1 |
Hippe PF CC 31 Woven Cotton Cloth Reinforced Phenolic Resin - Round, Molded Tube and Rod Used in mechanical, electrical and electronic applications. Fine weave (>30 threads per cm).Information provided by Hippe. |