Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 10% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 20% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 20% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 20% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 20% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 30% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 30% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 40% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 50% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, hot rolled and 1050°C mill-annealed plate Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, plate after 1000 hours at 650°C (1200°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, plate after 1000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, plate after 1000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, plate after 16000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, plate after 16000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, plate after 4000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, plate after 4000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, plate after 8000 hours at 760°C (1400°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, plate after 8000 hours at 870°C (1600°F) Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of .. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 700 °C |
0.000134 ohm-cm @Temperature 1290 °F |
|
Haynes Hastelloy® C-2000® alloy, flat products Nickel-chromium-molybdenum (Ni-Cr-Mo) C-type alloys have a long history of use in the Chemical Process Industries and are known for their versatility. Not only do they resist all acids (especially h.. |
|||
Electrical Resistivity | 0.000134 ohm-cm | 0.000134 ohm-cm | Temperature Coefficient of 0.00001/K |
Goodfellow Evanohm® Precision Resistance Nickel Alloy Electrical resistance alloy with a very low temperature coefficient of resistivityInformation provided by Goodfellow. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 40% cold reduction, 1010°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 50% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 10% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 10% cold reduction, 1065°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C (1500°F), good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a var.. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 10% cold reduction, 1120°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 10% cold reduction, 1175°C anneal for 5 minutes Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |
|||
Electrical Resistivity | 0.000134 ohm-cm @Temperature 200 °C |
0.000134 ohm-cm @Temperature 392 °F |
|
Haynes 625 alloy, 40% cold reduction Cb and Ta content 3.7% combined. Excellent strength up to 816°C, good oxidation resistance and aqueous corrosion, excellent forming and welding characteristics. Applications include a variety of hi.. |