Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 2.70e+9 - 1.00e+12 ohm-cm | 2.70e+9 - 1.00e+12 ohm-cm | Average value: 3.01e+11 ohm-cm Grade Count:4 |
Overview of materials for Thermoplastic Polyurethane, Elastomer, Ether Grade This property data is a summary of similar materials in the MatWeb database for the category "Thermoplastic Polyurethane, Elastomer, Ether Grade". Each property range of values reported is minimum a.. |
|||
Electrical Resistivity | 0.0100 - 1.00e+12 ohm-cm | 0.0100 - 1.00e+12 ohm-cm | Average value: 1.03e+10 ohm-cm Grade Count:59 |
Overview of materials for Polycarbonate, Carbon Fiber Reinforced This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Carbon Fiber Reinforced". Each property range of values reported is minimum and maximum v.. |
|||
Electrical Resistivity | 0.100 - 1.00e+12 ohm-cm | 0.100 - 1.00e+12 ohm-cm | Average value: 1.58e+10 ohm-cm Grade Count:64 |
Overview of materials for Polycarbonate, Stainless Steel Fiber This property data is a summary of similar materials in the MatWeb database for the category "Polycarbonate, Stainless Steel Fiber". Each property range of values reported is minimum and maximum val.. |
|||
Electrical Resistivity | 2.20e+10 - 1.00e+12 ohm-cm | 2.20e+10 - 1.00e+12 ohm-cm | Average value: 7.55e+11 ohm-cm Grade Count:8 |
Overview of materials for Phenolic, Novolac, Mineral/Fiber Filled This property data is a summary of similar materials in the MatWeb database for the category "Phenolic, Novolac, Mineral/Fiber Filled". Each property range of values reported is minimum and maximum .. |
|||
Electrical Resistivity | 5.00e+9 - 1.00e+12 ohm-cm | 5.00e+9 - 1.00e+12 ohm-cm | Average value: 4.33e+11 ohm-cm Grade Count:5 |
Overview of materials for Nylon 11, Flexible Tubing Grade This property data is a summary of similar materials in the MatWeb database for the category "Nylon 11, Flexible Tubing Grade". Each property range of values reported is minimum and maximum values o.. |
|||
Electrical Resistivity | 1.00e+8 - 1.00e+12 ohm-cm | 1.00e+8 - 1.00e+12 ohm-cm | undoped |
Mateck Zinc Sulphide, ZnS Semiconductor single crystals. Twins and stacking faults < 4% of hexagonal phase. |
|||
Electrical Resistivity | 1.00e+6 - 1.00e+12 ohm-cm | 1.00e+6 - 1.00e+12 ohm-cm | |
BACT DLC Diamond-Like Coating DLC (a-C:H). This coating provides the highest hardness and abrasion resistance of the BACT products. Typical applications include high wear environments involving seals, molds, metal forming, and.. |
|||
Electrical Resistivity | 1.00e+8 - 1.00e+12 ohm-cm | 1.00e+8 - 1.00e+12 ohm-cm | |
BACT Dylyn® Diamond-Like Nanocomposite Coating a-C:H/a-Si:O nanocomposite. This coating provides the lowest friction of the BACT products, even in high humidity or wet environments. It offers an excellent combination of anti-stick and wear be.. |
|||
Electrical Resistivity | 1.00e+10 - 1.00e+12 ohm-cm | 1.00e+10 - 1.00e+12 ohm-cm | |
Goodfellow Cellophane, Rayophane Regenerated Cellulose Fiber All forms of cellulose degrade before they melt but natural cellulose can be regenerated by the xanthate process to manufacture fibres, commonly called rayon or viscose, and film, commonly called by.. |
|||
Electrical Resistivity | 1.00e+10 - 1.00e+12 ohm-cm | 1.00e+10 - 1.00e+12 ohm-cm | |
Goodfellow Cellophane, Rayophane Regenerated Cellulose Film All forms of cellulose degrade before they melt but natural cellulose can be regenerated by the xanthate process to manufacture fibres, commonly called rayon or viscose, and film, commonly called by.. |
|||
Electrical Resistivity | 1.00e+8 - 1.00e+12 ohm-cm | 1.00e+8 - 1.00e+12 ohm-cm | undoped |
Mateck Zinc Selenide, ZnSe Semiconductor single crystals. Twins and stacking faults twin free. |