Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 0% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 10% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 10% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 10% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 10% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 30% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 30% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 40% cold reduction, 1010°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 50% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, all-weld metal GTAW Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, bar after 16000 hours at 537°C Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 0 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 1000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 650°C (1200°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 8000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, cold rolled, solution annealed sheet, 0.8-2.8 mm thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, hot rolled, solution annealed plate, 6.4-12.7 mm (1/2 in.) thick Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, sheet after 1000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm | 0.000119 ohm-cm | |
Carlson C 601 Nickel-Chromium-Iron Alloy General DescriptionCarlson Alloy C 6021 is a nickel-chromium alloy, developed specifically for high –temperature service. This alloy exhibits outstanding resistance to both cyclic and static oxida.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 20% cold reduction Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 20% cold reduction, 1121°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, 50% cold reduction, 1065°C anneal for 5 minutes Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, bar after 16000 hours at 760°C (1400°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, sheet after 1000 hours at 871°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |
|||
Electrical Resistivity | 0.000119 ohm-cm @Temperature 800 °C |
0.000119 ohm-cm @Temperature 1470 °F |
|
Haynes 556® alloy, bar, after 4000 hours at 870°C (1600°F) Effective resistance to sulfidizing, carburizing, and chlorine-bearing environments at high temperature; good oxidation resistance, fabricability, and excellent high-temperature strength; resists co.. |