Electrical Properties | Metric | English | Comments |
---|---|---|---|
Electrical Resistivity | 0.0000910 ohm-cm | 0.0000910 ohm-cm | |
Outokumpu 4742 High Temperature Ferritic Stainless Steel Good scaling resistance and can be subjected to reducing sulphur environments without risk. Subject to 475°C embrittlement and grain coarsening at temperatures above 950°C. s-phase may form afte.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm | 0.0000910 ohm-cm | |
Pyramid Stainless Steel AISI 304/316L, STAINLESS STEEL SHEET NO.4 FINISH Information provided by Pyramid Stainless Steel Ind Co Ltd |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 1.6 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 12.7 mm (1/2 in.) thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, 15.9 mm thick bar Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.0 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 1.7 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 15.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 4.8 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 7.9 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 3.2 mm thick sheet Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |
|||
Electrical Resistivity | 0.0000910 ohm-cm | 0.0000910 ohm-cm | |
Special Metals INCOLOY® A-286 Iron-Nickel-Chromium Alloy Data provided by the manufacturer, Special Metals. |
|||
Electrical Resistivity | 0.0000910 ohm-cm | 0.0000910 ohm-cm | |
ATI Allegheny Ludlum Altemp® A286 Iron-Base Superalloy, UNS S66286 Allegheny Ludlum Altemp A286 alloy is an iron-base superalloy useful for applications requiring high strength and corrosion resistance up to 704 degrees Celsius and for lower stress applications at .. |
|||
Electrical Resistivity | 0.0000910 ohm-cm @Temperature 22.0 °C |
0.0000910 ohm-cm @Temperature 71.6 °F |
|
Kennametal Stellite Stellite® 6B solution heat-treated at 1232°C, air cooled, 11.1 mm thick plate, aged 3 hours at 816°C Machined with tungsten-carbide tools. Inherent wear resistance, resistant to the wearing effects of hard, sharp particles such as in screw conveyors, rock crushing rollers, tile-making machines, and.. |