- Polymer Property : Cure Time = 8.00 hour
Polymer Property : Cure Time = 8.00 hour Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 480 - 720 min @Temperature 80.0 °C |
8.00 - 12.0 hour @Temperature 176 °F |
|
| Resinlab® EP1285HD-12 Highly Filled, Medium Viscosity Casting Resin Resinlab™ EP1285 (Formerly Lab Product W021901 series) is a highly filled, medium viscosity black casting resin designed for applications requiring a high degree of thermal conductivity and a low C.. |
|||
| Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
De-mold Time |
| Northstar Polymers MPA-A30B Mold-Making Resin MPA-A30B is a room-temperature-cure liquid castable polyurethane system. This ether-base polyurethane system is used in applications such as mold-making, prototyping, production of cast parts, pott.. |
|||
| Cure Time | 480 - 540 min @Temperature 25.0 °C |
8.00 - 9.00 hour @Temperature 77.0 °F |
De-mold Time |
| Northstar Polymers MPP-D80B Rigid Polyurethane MPP-D80B has a high load-bearing property at hardness 80 D Durometer. This material has a relatively slow curing pattern. Whereas many polyurethane formulations of this hardness cure very fast thus.. |
|||
| Cure Time | 480 min @Temperature 82.2 °C |
8.00 hour @Temperature 180 °F |
Complete Cure Cycle |
| Northstar Polymers MSB-M25F Microcellular Foam based on High Performance Polyester Polyurethane This high performance polyester microcellular foam system is one of a family of polymer systems developed by Northstar Polymers for demanding work environments. Urethane foams molded with this syste.. |
|||
| Cure Time | 480 min @Temperature 93.3 °C |
8.00 hour @Temperature 200 °F |
|
| Lord Adhesives Thermosetâ„¢ LS 213-9 Unfilled Epoxy Encapsulant Lord LS 213-9 is a one component epoxy coating and impregnating compound featuring low viscosity, good moisture resistance and excellent dielectric properties. Typical applications include transform.. |
|||
| Cure Time | 480 min @Temperature 60.0 °C |
8.00 hour @Temperature 140 °F |
|
| Tra-Con Tra-Bond 724-17GR Polyurethane Adhesive TRA-BOND 724-17GR premixed and frozen, polyurethane adhesive is designed for good adhesion, providing strong resilient bonds to a wide variety of substrates, including aluminum, solder, nylon, mylar.. |
|||
| Cure Time | 480 min @Temperature 60.0 °C |
8.00 hour @Temperature 140 °F |
|
| Tra-Con Tra-Bond 724-5 Low Viscosity Polyurethane Adhesive TRA-BOND 724-5 is a premixed and frozen, electrically insulating, polyurethane adhesive. This resilient adhesive exhibits good adhesion to a wide variety of substrates, including aluminum, solder, n.. |
|||
| Cure Time | 480 min @Temperature 75.0 °C |
8.00 hour @Temperature 167 °F |
|
| Tra-Con Tra-Bond 832-5 Flexible Epoxy TRA-BOND 832-5 is a flexible two component epoxy which is intended for bonding materials with mis-matched coefficients of expansion. It exhibits flexibility associated with polyurethanes but does no.. |
|||
| Cure Time | 480 - 960 min @Temperature 25.0 °C |
8.00 - 16.0 hour @Temperature 77.0 °F |
|
| Trelleborg Emerson & Cuming Eccobond® 24 LV General Purpose Catalyst Emerson & Cuming 24 LV Eccobond® General Purpose CatalystFaster curing, shorter working life version of 23 LV. Recommended for small mass castings due to higher exotherm. Cure Type: Room Temp or He.. |
|||
| Cure Time | 480 - 720 min @Temperature 65.6 °C |
8.00 - 12.0 hour @Temperature 150 °F |
|
| Master Bond EP29LPSP Low Outgassing, Optically Clear Two Component Epoxy Master Bond Polymer System EP29LPSP is a two component, high performance, modified low temperature heat cured epoxy system specially formulated for cryogenic applications. EP29LPSP is serviceable at.. |
|||
| Cure Time | 480 min @Temperature 4.00 °C |
8.00 hour @Temperature 39.2 °F |
Full Chemical |
| Chesterton ARC 5 Paste grade Rapid Cure Abrasion Control Description: ARC 5 is an advanced composite formulated for emergency repair and patching of metal components subject to light abrasive and corrosive conditions. It can be used to seal leaks and patc.. |
|||
| Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
Light Load |
| Chesterton ARC 890 Course Grade Sliding Wear Compound An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at the thickness of 6 mm (1/4”).. |
|||
| Cure Time | 480 min @Temperature 16.0 °C |
8.00 hour @Temperature 60.8 °F |
Light Load |
| Chesterton ARC 988 Composite Description: A high performance, quartz reinforced composite designed to resurface and restore concrete surfaces, to protect new concrete, and to repair concrete damaged by severe chemical and physi.. |
|||
| Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
Light Load |
| Chesterton ARC I BX1 Impact & Wear Resistant Epoxy Composite Description: An advanced grade epoxy and urethane composite for the repair and protection of all metal surfaces subjected to severe abrasion and impact. It is normally applied at a thickness of 6 mm.. |
|||
| Cure Time | 480 min @Temperature 16.0 °C |
8.00 hour @Temperature 60.8 °F |
Tack Free |
| Chesterton ARC MXHT High temperature severe wear compound Description: An advanced ceramic composite for the protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack at elevated temperatures. It is applied at a thickness o.. |
|||
| Cure Time | 480 min @Temperature 80.0 °C |
8.00 hour @Temperature 176 °F |
|
| Cytec EN-11 (Conap) Casting, Potting, and Molding Compound High Technology Potting, Casting and Molding CompoundsTwo-component, polybutadiene-based liquid urethane casting and potting systems. When reacted these high technology systems produce tough, stable.. |
|||
| Cure Time | 480 - 720 min @Temperature 25.0 °C |
8.00 - 12.0 hour @Temperature 77.0 °F |
|
| Epoxyset Epoxiohm EO-30FST Electrically Conductive Epoxy Adhesive EO-30-FST is two part, fast cure, silver filled, and high electrical conductivity epoxy adhesive. Both components are silver filled permitting a simple 1:1 mix ratio by weight. It has smooth creamy .. |
|||
| Cure Time | 480 min @Temperature 10.0 °C |
8.00 hour @Temperature 50.0 °F |
Overcoat Begin |
| Chesterton ARC HT-S High Temperature Corrosion Resistant Coating Description: ARC HT-S is a high temperature corrosion resistant coating for continuous operating conditions at elevated temperatures. It is easily applied by brush or roller and can be sprayed with .. |
|||
| Cure Time | 480 min @Temperature 4.00 °C |
8.00 hour @Temperature 39.2 °F |
Full Chemical |
| Chesterton MRS 5 Metal Rebuilding System MRS 5 is an advanced composite formulated for emergency repair and patching of metal components subject to light abrasive and corrosive conditions. It can be used to seal leaks and patch holes as we.. |
|||
| Cure Time | 480 - 660 min @Temperature 22.0 °C |
8.00 - 11.0 hour @Temperature 71.6 °F |
|
| Dow Corning 3-4241 DIELECTRIC TOUGH GEL KIT Two-part, translucent green, RT or heat cure, UV indicator, long working time, tough primerless chemical adhesion, UL 94 V-1 flammability classification.Information provided by Dow Corning |
|||
| Cure Time | 480 min @Temperature 4.40 °C |
8.00 hour @Temperature 39.9 °F |
|
| 3M AC-250 A-1/6 Aerospace Sealant 3M Aerospace Sealant AC-250 A-1/6 is a two-part, low temperature curing polysulfide, quick repair sealant for integral fuel tank and fuselage sealing applications. The mixed compound is a pourable l.. |
|||
| Cure Time | 480 - 720 min @Temperature 24.0 °C |
8.00 - 12.0 hour @Temperature 75.2 °F |
demold time |
| BCC Products BC 8880 Polyurethane Elastomer Surface Coat BC8880 is a two-part urethane gel coat which exhibits excellent handling characteristics and very low moisture sensitivity. Its characteristics include a high modulus and a high hardness. It is a br.. |
|||
| Cure Time | 480 min @Temperature 60.0 °C |
8.00 hour @Temperature 140 °F |
|
| Tra-Con Tra-Bond 724-17GR1B3 Polyurethane Adhesive TRA-BOND 724-17GR1B3 premixed and frozen polyurethane adhesive is designed for good adhesion, providing strong resilient bonds to a wide variety of substrates, including aluminum, solder, nylon, myl.. |
|||
| Cure Time | 480 min @Temperature 75.0 °C |
8.00 hour @Temperature 167 °F |
|
| Tra-Con Tra-Bond 872-3 Flexible Epoxy Adhesive TRA-BOND 872-3 transparent, flexible epoxy adhesive is designed for bonding materials with mismatched coefficients of thermal expansion. The long working life of this adhesive makes it ideal for use.. |
|||
| Cure Time | 480 min @Temperature 25.0 °C |
8.00 hour @Temperature 77.0 °F |
Tack Free |
| Chesterton ARC S4+ 100% Novolac acid resistant coating Description: An advanced polymer composite formulated to protect equipment from extreme chemical attack and corrosion. It is typically applied by spray, roller or brush at a nominal thickness of 375.. |
|||