Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 420 - 600 min @Temperature 25.0 °C |
7.00 - 10.0 hour @Temperature 77.0 °F |
4 dry mils; tack free |
Lord Adhesives Aeroglaze® 9929 Epoxy Primer Aeroglaze® 9929 epoxy primer is designed to be used on properly prepared aluminum and steel surfaces for applications that require protection against corrosion.All information provided by Lord. |
|||
Cure Time | 420 min @Temperature 22.0 °C |
7.00 hour @Temperature 71.6 °F |
|
Dow Corning SE 4430 KIT Two-part, thermally conductive elastomer, soft, good thermal conducitvity, UL 94 V-0 rating, low viscosity.Information provided by Dow Corning |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Light Load |
Chesterton ARC 10 Paste grade machinable composite Description: A reinforced composite for the repair and protection of metal surfaces. It is machinable with excellent compressive strength, chemical resistance and corrosion resistance. It is non-sag.. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Light Load |
Chesterton ARC 858 Abrasion resistant rebuilding and faring composite An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 0.15 mm (60 mils) or m.. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Tack Free |
Chesterton ARC 890 Course Grade Sliding Wear Compound An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at the thickness of 6 mm (1/4”).. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Tack Free |
Chesterton ARC 897 Fine Grade Sliding Wear Compound Description: ARC 897 is an advanced ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a t.. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Tack Free |
Chesterton ARC BX1 Sliding Wear Compound Description: An advanced contractor grade ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at.. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Tack Free |
Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound Description: ARC BX2 is an advanced contractor grade ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It .. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Tack Free |
Chesterton ARC I BX1 Impact & Wear Resistant Epoxy Composite Description: An advanced grade epoxy and urethane composite for the repair and protection of all metal surfaces subjected to severe abrasion and impact. It is normally applied at a thickness of 6 mm.. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Light Load |
Chesterton ARC MX1 Vertical Build Extreme Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It is applied at a thickness of 6 mm (1/4”).. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Tack Free |
Chesterton ARC PW Potable Water Coating Description: ARC PW is a 100% solids lining certified for NSF/ANSI 61 potable water, cold water service. It is recommended to be applied by brush, roll or spray at 500-750 microns (20-30 mils) total.. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Tack Free |
Chesterton ARC S1 General purpose coating Description: An advanced polymer composite formulated to protect metal surfaces from corrosion and chmical attack. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrink.. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Tack Free |
Chesterton ARC MX2 High Wear Fine Particle Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”.. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Light Load |
Chesterton ARC MXC Castable Extreme Wear Compound Description: An advanced ceramic composite, with flowable viscosity, for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It can be hand tro.. |
|||
Cure Time | 420 min @Temperature 4.40 °C |
7.00 hour @Temperature 39.9 °F |
Tack-Free Time |
3M AC-250 A-1/6 Aerospace Sealant 3M Aerospace Sealant AC-250 A-1/6 is a two-part, low temperature curing polysulfide, quick repair sealant for integral fuel tank and fuselage sealing applications. The mixed compound is a pourable l.. |
|||
Cure Time | 420 min @Temperature 5.00 °C |
7.00 hour @Temperature 41.0 °F |
Dry to Touch Time; ASTM D1640 clause 7.5.2 |
3M Scotchkote™ 323 Purple Patch Compound 3M Scotchkote 323 Purple Patch Compound is an ambient temperature cure, two-part system designed to protect metal, concrete and other surfaces from corrosion and deterioration. Scotchkote 323 Purple.. |
|||
Cure Time | 420 min @Temperature 5.00 °C |
7.00 hour @Temperature 41.0 °F |
ASTM D1640 |
3M Scotchkote™ 323R Liquid Epoxy Coating 3M Scotchkote Rebar Liquid Patch Compound 323R is a two-part, ambient temperature cure, 100% solids content, thermosetting, liquid epoxy coating. Intended Uses:As a patch materialAs a rebar shear en.. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Light Load |
Chesterton MRS 10 Metal Rebuilding System Description: A reinforced composite for the repair and protection of metal surfaces. It is machinable with excellent compressive strength, chemical resistance It is non-sagging, non-shrinking and 10.. |
|||
Cure Time | 420 min @Temperature 16.0 °C |
7.00 hour @Temperature 60.8 °F |
Light Load |
Chesterton MRS 58 Metal Rebuilding System An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 1.5 mm (60 mils) or mo.. |
|||
Cure Time | 420 min @Temperature 23.0 °C |
7.00 hour @Temperature 73.4 °F |
Zinc, working strength |
Permabond A136 Anaerobic Gasketmaker Permabond® A136 is an anaerobic material designed for making 'formed in situ' gaskets between metal surfaces. It is capable of replacing a wide range of conventional gaskets thereby offering potent.. |
|||
Cure Time | 420 min @Temperature 25.0 °C |
7.00 hour @Temperature 77.0 °F |
Tack Free |
Chesterton ARC S1HB Sprayable high-viscosity, 100% solids, advanced coating An advanced composite formulated to protect concrete and metal surfaces from corrosion and chemical attack. It is normally applied at a thickness of 1-2 mm (40-80 mils) per coat. However, greater si.. |