Polymer Property : Cure Time = 48.0 hour Product List

Processing Properties

Tips: 30 items are displayed at most. For the rest of the results, please contact customer service.

Processing Properties	Metric	English	Comments
Cure Time	2880 min @Temperature 25.0 °C	48.0 hour @Temperature 77.0 °F	Complete Cure Cycle
Northstar Polymers MPP-A60A Liquid Castable Polyurethane MPP-A60A is a room-temperature-cure liquid castable polyurethane system. This ether-base polyurethane system is used in applications such as mold-making, prototyping, production of cast parts, pott..
Cure Time	2880 min @Temperature 25.0 °C	48.0 hour @Temperature 77.0 °F	Complete Cure Cycle
Northstar Polymers MPS-M23B Room-Temperature Curable Microcellular Foam This foam polyurethane formulation is designed to yield closed-cell microcellular foam by either hand-mixing or machine casting method at room temperature. The components are liquid at room temperat..
Cure Time	2880 min @Temperature 25.0 °C	48.0 hour @Temperature 77.0 °F
Resin Technology Group TIGA 291-EX Grey Medium Viscosity Polyamide Epoxy Adhesive Mix ratio 1 to 1 by weight.Tiga 291 EX Grey is a medium viscosity polyamide/ epoxy adhesive recommended for bonding applications where high shock impact resistance and peel resistance are desired. T..
Cure Time	2880 - 10100 min @Temperature 23.0 °C	48.0 - 168 hour @Temperature 73.4 °F
Resin Technology Group UV MX-2240 Multi-Functional Hybrid, UV-Curing, Micro-Electronic System Mix ratio 2 to 1 by volume.UV-MX 2240 is a low-viscosity, water-white photo/ chemical cross-linking encapsulant/sealant designed for micro-electronic applications. This two-part, Hybrid UV-epoxy bas..
Cure Time	2880 - 4320 min @Temperature 23.9 °C	48.0 - 72.0 hour @Temperature 75.0 °F
Master Bond EP21ANHT Two Component, Room Temperature Curing Epoxy Adhesive Product Description: Master Bond Polymer Adhesive EP21ANHT is a two component room temperature curing adhesive, sealant and coating that combines high thermal conductivity and electrical insulation ..
Cure Time	2880 - 4320 min @Temperature 23.9 °C	48.0 - 72.0 hour @Temperature 75.0 °F
Master Bond EP21HTND High Temperature Resistant, Non-Drip Epoxy Compound Description: Master Bond EP21HTND is a two component, room temperature curing epoxy adhesive, sealant and coating with a paste viscosity and non-drip application feature. Its features are easy handl..
Cure Time	2880 - 4320 min @Temperature 23.9 °C	48.0 - 72.0 hour @Temperature 75.0 °F
Master Bond EP21NDFG Two component epoxy compound for high performance applications Product Description: Master Bond EP21NDFG is a two component, room temperature curing epoxy adhesive featuring outstanding physical properties, easy processing and a non-drip, paste-like consistency..
Cure Time	2880 - 4320 min @Temperature 23.9 °C	48.0 - 72.0 hour @Temperature 75.0 °F
Master Bond EP21TDC-2ND Two component, highly flexibilized, non-drip epoxy resin compound Product Description: Master Bond EP21TDC-2ND is a two component highly flexible epoxy resin system for high performance bonding, sealing and coating with a non-drip consistency. It has a forgiving o..
Cure Time	2880 - 3600 min @Temperature 23.0 °C	48.0 - 60.0 hour @Temperature 73.4 °F
Master Bond EP21TPND Non Drip Polysulfide Based Two Component Adhesive System Master Bond Polymer Adhesive EP21TPND is a two component polysulfide/epoxy based adhesive/sealant formulated to cure at room temperature or more rapidly at elevated temperatures, with a 100 to 100 m..
Cure Time	2880 - 4320 min @Temperature 23.9 °C	48.0 - 72.0 hour @Temperature 75.0 °F
Master Bond EP30AN-1 Low Viscosity, NASA Low Outgassing Epoxy Description: Master Bond EP30AN-1 is a two part epoxy for high performance potting, sealing, coating and bonding featuring high thermal conductivity, excellent electrical insulation properties and N..
Cure Time	2880 - 5760 min @Temperature 23.0 °C	48.0 - 96.0 hour @Temperature 73.4 °F
Master Bond EP21TDC-7 Highly Flexible Two Component Epoxy System Master Bond Polymer System EP21TDC-7 is a two component highly flexible epoxy resin system for high performance bonding, sealing, and coating. It is formulated to cure at ambient temperatures or mor..
Cure Time	2880 - 4320 min @Temperature 23.9 °C	48.0 - 72.0 hour @Temperature 75.0 °F
Master Bond Supreme 33 High Temperature Resistant, Structural Adhesive Description: Master Bond Polymer System Supreme 33 is a unique, room temperature curing, toughened epoxy adhesive/sealant, offering high temperature resistance. This innovative system offers high bo..
Cure Time	2880 min @Temperature 10.0 °C	48.0 hour @Temperature 50.0 °F	Full Load
Chesterton ARC 10 Paste grade machinable composite Description: A reinforced composite for the repair and protection of metal surfaces. It is machinable with excellent compressive strength, chemical resistance and corrosion resistance. It is non-sag..
Cure Time	2880 min @Temperature 10.0 °C	48.0 hour @Temperature 50.0 °F	Full Load
Chesterton ARC 858 Abrasion resistant rebuilding and faring composite An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 0.15 mm (60 mils) or m..
Cure Time	2880 min @Temperature 16.0 °C	48.0 hour @Temperature 60.8 °F	Full Load
Chesterton ARC 890 Course Grade Sliding Wear Compound An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at the thickness of 6 mm (1/4”)..
Cure Time	2880 min @Temperature 16.0 °C	48.0 hour @Temperature 60.8 °F	Full Load
Chesterton ARC 982 100% Novolac acid resistant coating Description: An advanced polymer composite formulated to protect equipment from extreme chemical attack and corrosion. A low viscosity composite that is applied by brush, squeegee, or a plural compo..
Cure Time	2880 min @Temperature 25.0 °C	48.0 hour @Temperature 77.0 °F	Full Chemical
Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound Description: ARC BX2 is an advanced contractor grade ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It ..
Cure Time	2880 min @Temperature 16.0 °C	48.0 hour @Temperature 60.8 °F	Full Load
Chesterton ARC PW Potable Water Coating Description: ARC PW is a 100% solids lining certified for NSF/ANSI 61 potable water, cold water service. It is recommended to be applied by brush, roll or spray at 500-750 microns (20-30 mils) total..
Cure Time	2880 min @Temperature 25.0 °C	48.0 hour @Temperature 77.0 °F	Full Chemical
Chesterton ARC SD4i High temperature ceramic reinforced erosion resistant coating Description: An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10-15 mils) per coat..
Cure Time	2880 min @Temperature 16.0 °C	48.0 hour @Temperature 60.8 °F	Full Load
Chesterton MRS SD4i Metal Rebuilding System An advanced ceramic composite for resurfacing and protection of metal surfaces in immersion service. It is normally applied in a thickness range of 250-370 microns (10 – 15 mils) per coat. Non-shri..
Cure Time	2880 min @Temperature 23.0 °C	48.0 hour @Temperature 73.4 °F	minimum
Epoxy Technology EPO-TEK® OE121 Black Epoxy Adhesive Material Description: A two component, low temperature curing epoxy adhesive designed for semiconductor flip chip underfill. It is color coded black for visual ID during the underfilling process. ..
Cure Time	2880 min @Temperature 23.0 °C	48.0 hour @Temperature 73.4 °F	Minimum
Epoxy Technology EPO-TEK® T7109-18 Electrically Insulating Epoxy Paste Material Description: A flexible, electrically insulating epoxy paste designed for low stress and heat dissipation applications. Alternative to EPO-TEK® T7109-17.Information Provided by Epoxy Tec..
Cure Time	2880 min @Temperature 16.0 °C	48.0 hour @Temperature 60.8 °F	Full Load
Chesterton ARC MX2 High Wear Fine Particle Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”..
Cure Time	2880 min @Temperature 25.0 °C	48.0 hour @Temperature 77.0 °F	Full Chemical
Chesterton ARC MX2 High Wear Fine Particle Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”..