- Polymer Property : Cure Time = 12.0 hour
Polymer Property : Cure Time = 12.0 hour Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 720 - 1200 min @Temperature 25.0 °C |
12.0 - 20.0 hour @Temperature 77.0 °F |
|
| Resin Technology Group TIGA 202-EX High Performance, Fast Cure Adhesive Mix ratio 2 to 1 by volume.TIGA 202-EX is a two-part epoxy adhesive offering outstanding shear tensile and peel adhesion. TIGA 202-EX offers a 20 minute pot life and good hardness development within.. |
|||
| Cure Time | 720 min @Temperature 25.0 °C |
12.0 hour @Temperature 77.0 °F |
Permit Handling |
| Lord Adhesives Aeroglaze® Z302 Absorptive Polyurethane Aeroglaze® Z302 absorptive polyurethane is primarily for application to substrates used in space operations. These operations include those where coatings must exhibit low outgassing characterist.. |
|||
| Cure Time | 720 min @Temperature 25.0 °C |
12.0 hour @Temperature 77.0 °F |
Permit Handling |
| Lord Adhesives Aeroglaze® Z306 Absorptive Polyurethane Aeroglaze® Z306 absorptive polyurethane coating is primarily for applications to substrates used in space operations. These operations include those where coatings must exhibit low outgassing cha.. |
|||
| Cure Time | 720 - 960 min @Temperature 80.0 - 90.0 °C |
12.0 - 16.0 hour @Temperature 176 - 194 °F |
|
| Lord Adhesives Thermosetâ„¢ EP-809 Ignition Coil Impregnating and Encapsulation Epoxy Lord EP-809 is a long working life, heat curing, two component epoxy formulation. It was designed especially for potting high voltage automotive ignition coils. The combination of low viscosity, exc.. |
|||
| Cure Time | 720 - 1440 min @Temperature 23.9 °C |
12.0 - 24.0 hour @Temperature 75.0 °F |
plus 2 hrs at 150-200°F |
| Master Bond EP21LV-LO Two Component, Lower Viscosity, Room Temperature Curing Epoxy System Product Description: Master Bond EP21LV-LO is a two component, lower viscosity, room temperature curing epoxy system for high performance bonding, sealing, coating and encapsulation. This user frien.. |
|||
| Cure Time | 720 min @Temperature 23.9 °C |
12.0 hour @Temperature 75.0 °F |
Followed by 2-3 hours at 150-200°F (Optimum Cure Schedule) |
| Master Bond EP21TDC-4ND Two component, highly flexibilized epoxy for bonding, sealing and coating Product Description: Master Bond EP21TDC-4ND is a two component, very flexible epoxy system for high performance bonding, sealing and coating with a non-drip consistency. It has a one to four mix ra.. |
|||
| Cure Time | 720 min @Temperature 23.9 °C |
12.0 hour @Temperature 75.0 °F |
Followed by 2-3 hours at 150-200°F (Optimum Cure Schedule) |
| Master Bond EP21TDCHTND Versatile, toughened two component epoxy for bonding, sealing and coating Product Description: Master Bond EP21TDCHTND is a two component epoxy adhesive, sealant and coating featuring high performance, versatility and exceptional user friendliness. It has a very forgiving.. |
|||
| Cure Time | 720 min @Temperature 50.0 °C |
12.0 hour @Temperature 122 °F |
|
| Tra-Con Tra-Duct 29121 Snap Cure Conductive Silver Epoxy Adhesive TRA-DUCT 29121 is 100% solids, two component silver filled epoxy designed for chip bonding in microelectronic and optoelectronic applications. TRA-DUCT 29121 is a soft, smooth paste. This two-part f.. |
|||
| Cure Time | 720 min @Temperature 50.0 °C |
12.0 hour @Temperature 122 °F |
|
| Tra-Con Tra-Duct 925M01 Low Ion Snap Cure Silver-Filled Epoxy TRA-DUCT 925M01 is a low ion snap cure silver-filled epoxy. TRA-DUCT 925M01 develops strong, durable, void free electrically and thermally conducting bonds. The product can be screen printed, stenci.. |
|||
| Cure Time | 720 - 1440 min @Temperature 23.0 °C |
12.0 - 24.0 hour @Temperature 73.4 °F |
|
| Master Bond EP27 Low Temperature Curing Two Component Epoxy Master Bond Polymer System EP27 is a unique two component
epoxy formulation offers relatively fast cures at temperatures as low as 40°F and below, with curing times much shorter than currently exis.. |
|||
| Cure Time | 720 min @Temperature 65.6 - 93.3 °C |
12.0 hour @Temperature 150 - 200 °F |
followed by 2-3 hrs at 150°-200°F |
| Master Bond EP42HT-2FG Two Component Epoxy Adhesive for Food Applications Master Bond Polymer System EP42HT-2FG is a room temperature setting, two component epoxy adhesive, sealant and coating specially formulated for food applications. It has been independently tested an.. |
|||
| Cure Time | 720 min @Temperature 32.0 °C |
12.0 hour @Temperature 89.6 °F |
Full Load |
| Chesterton ARC 855 Abrasion Control Liquid Description: An advanced ceramic composite formulated to protect equipment from aggressive chemical attack, corrosion, and erosion. The product is a low viscosity composite that is easily applied by.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC 858 Abrasion resistant rebuilding and faring composite An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 0.15 mm (60 mils) or m.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC 890 Course Grade Sliding Wear Compound An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at the thickness of 6 mm (1/4”).. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC 897 Fine Grade Sliding Wear Compound Description: ARC 897 is an advanced ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a t.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC BX1 Sliding Wear Compound Description: An advanced contractor grade ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound Description: ARC BX2 is an advanced contractor grade ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It .. |
|||
| Cure Time | 720 min @Temperature 16.0 °C |
12.0 hour @Temperature 60.8 °F |
Foot Traffic |
| Chesterton ARC CS4 low-viscosity, 100% solids, barrier coating Description: An advanced composite formulated to protect concrete surfaces from harsh chemical attack. It is normally applied at a thickness of 250-375 microns (10-15 mils) per coat in a 2 coat syst.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC I BX1 Impact & Wear Resistant Epoxy Composite Description: An advanced grade epoxy and urethane composite for the repair and protection of all metal surfaces subjected to severe abrasion and impact. It is normally applied at a thickness of 6 mm.. |
|||
| Cure Time | 720 min @Temperature 32.0 °C |
12.0 hour @Temperature 89.6 °F |
Light Load |
| Chesterton ARC PW Potable Water Coating Description: ARC PW is a 100% solids lining certified for NSF/ANSI 61 potable water, cold water service. It is recommended to be applied by brush, roll or spray at 500-750 microns (20-30 mils) total.. |
|||
| Cure Time | 720 min @Temperature 32.0 °C |
12.0 hour @Temperature 89.6 °F |
Light Load |
| Chesterton ARC S1 General purpose coating Description: An advanced polymer composite formulated to protect metal surfaces from corrosion and chmical attack. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrink.. |
|||
| Cure Time | 720 min @Temperature 32.0 °C |
12.0 hour @Temperature 89.6 °F |
Overcoat End |
| Chesterton ARC HT-S High Temperature Corrosion Resistant Coating Description: ARC HT-S is a high temperature corrosion resistant coating for continuous operating conditions at elevated temperatures. It is easily applied by brush or roller and can be sprayed with .. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC MX2 High Wear Fine Particle Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Chemical |
| Chesterton ARC MX5 Rapid Curing Fine Particle Wear Compound Description: An advanced ceramic reinforced composite for the emergency repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a th.. |
|||
| Cure Time | 720 min @Temperature 75.0 °C |
12.0 hour @Temperature 167 °F |
Dust Free, at 50% humidity |
| Blue River Coatings CRC100-H BLUE RIVER COATINGS CRC100-H is a two-component inorganic corrosion resistant coating designed for Original Equipment Manufacturers (OEM) to protect metal substrates from corrosion and abrasion. If .. |
|||
| Cure Time | 720 - 1080 min @Temperature 24.0 °C |
12.0 - 18.0 hour @Temperature 75.2 °F |
|
| BCC Products BC 7053 Epoxy Casting BC 7053 is an iron filled epoxy casting system. This system is a high iron content material that provides unsurpassed wear resistance. BC7053 was designed for use in constructing core boxes, holding.. |
|||
| Cure Time | 720 min @Temperature 16.0 °C |
12.0 hour @Temperature 60.8 °F |
Foot Traffic |
| Chesterton ARC CS2 Low-viscosity, Composite concrete primer sealer Description: An advanced composite formulated to protect concrete surfaces from mild chemical attack. It is normally applied at a thickness of 250-375 microns (10-15 mils) per coat. Non-shrinking. 1.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton MRS 58 Metal Rebuilding System An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 1.5 mm (60 mils) or mo.. |
|||
| Cure Time | 720 - 960 min @Temperature 22.0 °C |
12.0 - 16.0 hour @Temperature 71.6 °F |
|
| Aremco Ceramacast™ 905 Silicon-Ceramic Potting Compound Ceramacast™ 905 is a silicone-bonded, ceramic filled high temperature adhesive and potting compound. |
|||