- Polymer Property : Cure Time = 720 min
Polymer Property : Cure Time = 720 min Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Cure Time | 720 - 1080 min @Temperature 25.0 °C |
12.0 - 18.0 hour @Temperature 77.0 °F |
|
| Resin Technology Group KONA 871 Low Cost Epoxy Resin Mix ratio 100 to 25 by weight.Kona 871 is a low cost epoxy resin system developed for production casting, potting, encapsulating and coating applications where easy handling, good flowability and lo.. |
|||
| Cure Time | 720 min @Temperature 25.0 °C |
12.0 hour @Temperature 77.0 °F |
Permit Handling |
| Lord Adhesives Aeroglaze® Z307 Absorptive Conductive Polyurethane Aeroglaze® Z307 black absorptive conductive polyurethane coating is primarily for application to substrates used on spacecraft. These applications include those where coatings must exhibit low ou.. |
|||
| Cure Time | 720 min @Temperature 23.9 °C |
12.0 hour @Temperature 75.0 °F |
followed by 2 hrs at 150-200°F |
| Master Bond EP21HTND High Temperature Resistant, Non-Drip Epoxy Compound Description: Master Bond EP21HTND is a two component, room temperature curing epoxy adhesive, sealant and coating with a paste viscosity and non-drip application feature. Its features are easy handl.. |
|||
| Cure Time | 720 - 1440 min @Temperature 23.9 °C |
12.0 - 24.0 hour @Temperature 75.0 °F |
plus 2 hrs at 150-200°F |
| Master Bond EP21LV-LO Two Component, Lower Viscosity, Room Temperature Curing Epoxy System Product Description: Master Bond EP21LV-LO is a two component, lower viscosity, room temperature curing epoxy system for high performance bonding, sealing, coating and encapsulation. This user frien.. |
|||
| Cure Time | 720 - 1440 min @Temperature 23.9 °C |
12.0 - 24.0 hour @Temperature 75.0 °F |
plus 2 hrs at 150-200°F |
| Master Bond EP21NDFG Two component epoxy compound for high performance applications Product Description: Master Bond EP21NDFG is a two component, room temperature curing epoxy adhesive featuring outstanding physical properties, easy processing and a non-drip, paste-like consistency.. |
|||
| Cure Time | 720 min @Temperature 23.9 °C |
12.0 hour @Temperature 75.0 °F |
Followed by 2-3 hours at 150-200°F (Optimum Cure Schedule) |
| Master Bond EP21TDC-2ND Two component, highly flexibilized, non-drip epoxy resin compound Product Description: Master Bond EP21TDC-2ND is a two component highly flexible epoxy resin system for high performance bonding, sealing and coating with a non-drip consistency. It has a forgiving o.. |
|||
| Cure Time | 720 min @Temperature 23.9 °C |
12.0 hour @Temperature 75.0 °F |
Followed by 2-3 hours at 150-200°F (Optimum Cure Schedule) |
| Master Bond EP21TDC-4ND Two component, highly flexibilized epoxy for bonding, sealing and coating Product Description: Master Bond EP21TDC-4ND is a two component, very flexible epoxy system for high performance bonding, sealing and coating with a non-drip consistency. It has a one to four mix ra.. |
|||
| Cure Time | 720 min @Temperature 23.0 °C |
12.0 hour @Temperature 73.4 °F |
|
| Master Bond EP24 Fast Curing Two Component Epoxy System Master Bond Polymer Adhesive EP24 is a fast curing two component epoxy adhesive for general purpose bonding, sealing, and coating formulated to cure at room temperature with a one-to-one mix ratio, .. |
|||
| Cure Time | 720 min @Temperature 23.9 °C |
12.0 hour @Temperature 75.0 °F |
followed by 1-2 hours at 150-200°F |
| Master Bond EP38CL Adhesive Features Toughness and Durability Description: Master Bond EP38CL is a lower viscosity, optically clear two component epoxy system for high performance bonding, coating, sealing and small encapsulations, featuring toughness and dura.. |
|||
| Cure Time | 720 - 1440 min @Temperature 23.9 °C |
12.0 - 24.0 hour @Temperature 75.0 °F |
|
| Master Bond EP51FL Toughened and Flexible Adhesive Compound Master Bond EP51FL is a two component epoxy system for high performance bonding sealing and coating. It combines superior toughness with user friendly handling properties, along with unusually fast .. |
|||
| Cure Time | 720 min @Temperature 50.0 °C |
12.0 hour @Temperature 122 °F |
|
| Tra-Con Tra-Duct 925M01 Low Ion Snap Cure Silver-Filled Epoxy TRA-DUCT 925M01 is a low ion snap cure silver-filled epoxy. TRA-DUCT 925M01 develops strong, durable, void free electrically and thermally conducting bonds. The product can be screen printed, stenci.. |
|||
| Cure Time | 720 - 1440 min @Temperature 23.0 °C |
12.0 - 24.0 hour @Temperature 73.4 °F |
|
| Master Bond EP27 Low Temperature Curing Two Component Epoxy Master Bond Polymer System EP27 is a unique two component
epoxy formulation offers relatively fast cures at temperatures as low as 40°F and below, with curing times much shorter than currently exis.. |
|||
| Cure Time | 720 min @Temperature 65.6 - 93.3 °C |
12.0 hour @Temperature 150 - 200 °F |
followed by 2-3 hrs at 150°-200°F |
| Master Bond EP42HT-2FG Two Component Epoxy Adhesive for Food Applications Master Bond Polymer System EP42HT-2FG is a room temperature setting, two component epoxy adhesive, sealant and coating specially formulated for food applications. It has been independently tested an.. |
|||
| Cure Time | 720 min @Temperature 25.0 °C |
12.0 hour @Temperature 77.0 °F |
Light Load |
| Chesterton ARC 855 Abrasion Control Liquid Description: An advanced ceramic composite formulated to protect equipment from aggressive chemical attack, corrosion, and erosion. The product is a low viscosity composite that is easily applied by.. |
|||
| Cure Time | 720 min @Temperature 32.0 °C |
12.0 hour @Temperature 89.6 °F |
Full Load |
| Chesterton ARC 855 Abrasion Control Liquid Description: An advanced ceramic composite formulated to protect equipment from aggressive chemical attack, corrosion, and erosion. The product is a low viscosity composite that is easily applied by.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC 858 Abrasion resistant rebuilding and faring composite An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 0.15 mm (60 mils) or m.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC 890 Course Grade Sliding Wear Compound An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at the thickness of 6 mm (1/4”).. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC BX1 Sliding Wear Compound Description: An advanced contractor grade ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound Description: ARC BX2 is an advanced contractor grade ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It .. |
|||
| Cure Time | 720 min @Temperature 16.0 °C |
12.0 hour @Temperature 60.8 °F |
Foot Traffic |
| Chesterton ARC CS4 low-viscosity, 100% solids, barrier coating Description: An advanced composite formulated to protect concrete surfaces from harsh chemical attack. It is normally applied at a thickness of 250-375 microns (10-15 mils) per coat in a 2 coat syst.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC I BX1 Impact & Wear Resistant Epoxy Composite Description: An advanced grade epoxy and urethane composite for the repair and protection of all metal surfaces subjected to severe abrasion and impact. It is normally applied at a thickness of 6 mm.. |
|||
| Cure Time | 720 min @Temperature 32.0 °C |
12.0 hour @Temperature 89.6 °F |
Light Load |
| Chesterton ARC S1 General purpose coating Description: An advanced polymer composite formulated to protect metal surfaces from corrosion and chmical attack. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrink.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton ARC MX2 High Wear Fine Particle Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Chemical |
| Chesterton ARC MX5 Rapid Curing Fine Particle Wear Compound Description: An advanced ceramic reinforced composite for the emergency repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a th.. |
|||
| Cure Time | 720 min @Temperature -6.70 °C |
12.0 hour @Temperature 19.9 °F |
Tack-Free Time |
| 3M AC-250 A-1/6 Aerospace Sealant 3M Aerospace Sealant AC-250 A-1/6 is a two-part, low temperature curing polysulfide, quick repair sealant for integral fuel tank and fuselage sealing applications. The mixed compound is a pourable l.. |
|||
| Cure Time | 720 - 1440 min @Temperature 23.0 °C |
12.0 - 24.0 hour @Temperature 73.4 °F |
Recommended Cure |
| Aremco Aremco-Bond™ 2220 High Performance Epoxide Ceramic-Filled, High Chemical Resistance, Machinable. For Repairing Deeply-Corroded Parts. |
|||
| Cure Time | 720 min @Temperature 75.0 °C |
12.0 hour @Temperature 167 °F |
Dust Free, at 50% humidity |
| Blue River Coatings CRC100-H BLUE RIVER COATINGS CRC100-H is a two-component inorganic corrosion resistant coating designed for Original Equipment Manufacturers (OEM) to protect metal substrates from corrosion and abrasion. If .. |
|||
| Cure Time | 720 - 1080 min @Temperature 24.0 °C |
12.0 - 18.0 hour @Temperature 75.2 °F |
|
| BCC Products BC 7053 Epoxy Casting BC 7053 is an iron filled epoxy casting system. This system is a high iron content material that provides unsurpassed wear resistance. BC7053 was designed for use in constructing core boxes, holding.. |
|||
| Cure Time | 720 min @Temperature 43.0 °C |
12.0 hour @Temperature 109 °F |
Full Load |
| Chesterton MRS 58 Metal Rebuilding System An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 1.5 mm (60 mils) or mo.. |
|||
| Cure Time | 720 - 960 min @Temperature 22.0 °C |
12.0 - 16.0 hour @Temperature 71.6 °F |
|
| Aremco Ceramacast™ 905 Silicon-Ceramic Potting Compound Ceramacast™ 905 is a silicone-bonded, ceramic filled high temperature adhesive and potting compound. |
|||