Processing Properties | Metric | English | Comments |
---|---|---|---|
Cure Time | 2160 - 2880 min @Temperature 25.0 °C |
36.0 - 48.0 hour @Temperature 77.0 °F |
Permit Normal Usage |
Lord Adhesives Aeroglaze® Z302 Absorptive Polyurethane Aeroglaze® Z302 absorptive polyurethane is primarily for application to substrates used in space operations. These operations include those where coatings must exhibit low outgassing characterist.. |
|||
Cure Time | 2160 - 2880 min @Temperature 25.0 °C |
36.0 - 48.0 hour @Temperature 77.0 °F |
Permit Normal Usage |
Lord Adhesives Aeroglaze® Z306 Absorptive Polyurethane Aeroglaze® Z306 absorptive polyurethane coating is primarily for applications to substrates used in space operations. These operations include those where coatings must exhibit low outgassing cha.. |
|||
Cure Time | 2160 - 2880 min @Temperature 25.0 °C |
36.0 - 48.0 hour @Temperature 77.0 °F |
Permit Normal Usage |
Lord Adhesives Aeroglaze® Z307 Absorptive Conductive Polyurethane Aeroglaze® Z307 black absorptive conductive polyurethane coating is primarily for application to substrates used on spacecraft. These applications include those where coatings must exhibit low ou.. |
|||
Cure Time | 2160 - 2880 min @Temperature 23.0 °C |
36.0 - 48.0 hour @Temperature 73.4 °F |
|
Master Bond EP30D-7 Flexibilized, Abrasion Resistant Epoxy System Master Bond Polymer System EP30D-7 is a versatile two component flexibilized, urethane-modified epoxy featuring superior strength, toughness and abrasion resistance for high performance bonding, sea.. |
|||
Cure Time | 2160 min @Temperature 25.0 °C |
36.0 hour @Temperature 77.0 °F |
Full Chemical |
Chesterton ARC 10 Paste grade machinable composite Description: A reinforced composite for the repair and protection of metal surfaces. It is machinable with excellent compressive strength, chemical resistance and corrosion resistance. It is non-sag.. |
|||
Cure Time | 2160 min @Temperature 10.0 °C |
36.0 hour @Temperature 50.0 °F |
Light Load |
Chesterton ARC 855 Abrasion Control Liquid Description: An advanced ceramic composite formulated to protect equipment from aggressive chemical attack, corrosion, and erosion. The product is a low viscosity composite that is easily applied by.. |
|||
Cure Time | 2160 min @Temperature 16.0 °C |
36.0 hour @Temperature 60.8 °F |
Full Load |
Chesterton ARC 858 Abrasion resistant rebuilding and faring composite An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 0.15 mm (60 mils) or m.. |
|||
Cure Time | 2160 min @Temperature 25.0 °C |
36.0 hour @Temperature 77.0 °F |
Full Chemical |
Chesterton ARC 858 Abrasion resistant rebuilding and faring composite An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 0.15 mm (60 mils) or m.. |
|||
Cure Time | 2160 min @Temperature 25.0 °C |
36.0 hour @Temperature 77.0 °F |
Full Chemical |
Chesterton ARC 890 Course Grade Sliding Wear Compound An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at the thickness of 6 mm (1/4”).. |
|||
Cure Time | 2160 min @Temperature 10.0 °C |
36.0 hour @Temperature 50.0 °F |
Light Load |
Chesterton ARC 897 Fine Grade Sliding Wear Compound Description: ARC 897 is an advanced ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a t.. |
|||
Cure Time | 2160 min @Temperature 25.0 °C |
36.0 hour @Temperature 77.0 °F |
Full Load |
Chesterton ARC 897 Fine Grade Sliding Wear Compound Description: ARC 897 is an advanced ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a t.. |
|||
Cure Time | 2160 min @Temperature 25.0 °C |
36.0 hour @Temperature 77.0 °F |
Full Chemical |
Chesterton ARC BX1 Sliding Wear Compound Description: An advanced contractor grade ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is normally applied at.. |
|||
Cure Time | 2160 min @Temperature 10.0 °C |
36.0 hour @Temperature 50.0 °F |
Light Load |
Chesterton ARC BX2 Contractor Grade Fine Sliding Wear Compound Description: ARC BX2 is an advanced contractor grade ceramic reinforced composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It .. |
|||
Cure Time | 2160 min @Temperature 32.0 °C |
36.0 hour @Temperature 89.6 °F |
Service |
Chesterton ARC HT-T Spark Testable High Temperature Trowelable Abrasion Control Compound An advanced ceramic composite formulated to protect equipment from corrosion and erosion in elevated temperature water solution immersion. This system is a high viscosity composite that is applied b.. |
|||
Cure Time | 2160 min @Temperature 16.0 °C |
36.0 hour @Temperature 60.8 °F |
Full Load |
Chesterton ARC MX1 Vertical Build Extreme Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It is applied at a thickness of 6 mm (1/4”).. |
|||
Cure Time | 2160 min @Temperature 10.0 °C |
36.0 hour @Temperature 50.0 °F |
Light Load |
Chesterton ARC PW Potable Water Coating Description: ARC PW is a 100% solids lining certified for NSF/ANSI 61 potable water, cold water service. It is recommended to be applied by brush, roll or spray at 500-750 microns (20-30 mils) total.. |
|||
Cure Time | 2160 min @Temperature 25.0 °C |
36.0 hour @Temperature 77.0 °F |
Full Load |
Chesterton ARC PW Potable Water Coating Description: ARC PW is a 100% solids lining certified for NSF/ANSI 61 potable water, cold water service. It is recommended to be applied by brush, roll or spray at 500-750 microns (20-30 mils) total.. |
|||
Cure Time | 2160 min @Temperature 10.0 °C |
36.0 hour @Temperature 50.0 °F |
Light Load |
Chesterton ARC S1 General purpose coating Description: An advanced polymer composite formulated to protect metal surfaces from corrosion and chmical attack. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrink.. |
|||
Cure Time | 2160 min @Temperature 16.0 °C |
36.0 hour @Temperature 60.8 °F |
Overcoat End |
Chesterton ARC S1 General purpose coating Description: An advanced polymer composite formulated to protect metal surfaces from corrosion and chmical attack. It is normally applied at a thickness of 250 microns (10 mils) per coat. Non-shrink.. |
|||
Cure Time | 2160 min @Temperature 10.0 °C |
36.0 hour @Temperature 50.0 °F |
Light Load |
Chesterton ARC MX2 High Wear Fine Particle Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”.. |
|||
Cure Time | 2160 min @Temperature 25.0 °C |
36.0 hour @Temperature 77.0 °F |
Full Load |
Chesterton ARC MX2 High Wear Fine Particle Wear Compound Description: An advanced ceramic composite for the repair and protection of all metal surfaces subjected to severe erosion, corrosion and chemical attack. It is applied at a thickness of 3 mm (1/8”.. |
|||
Cure Time | 2160 min @Temperature 16.0 °C |
36.0 hour @Temperature 60.8 °F |
Full Chemical |
Chesterton ARC MX5 Rapid Curing Fine Particle Wear Compound Description: An advanced ceramic reinforced composite for the emergency repair and protection of all metal surfaces subjected to severe erosion, corrosion, and chemical attack. It is applied at a th.. |
|||
Cure Time | 2160 min @Temperature 16.0 °C |
36.0 hour @Temperature 60.8 °F |
Full Load |
Chesterton ARC MXC Castable Extreme Wear Compound Description: An advanced ceramic composite, with flowable viscosity, for the repair and protection of all metal surfaces subjected to severe erosion, abrasion and chemical attack. It can be hand tro.. |
|||
Cure Time | >= 2160 min @Temperature 0.000 °C |
>= 36.0 hour @Temperature 32.0 °F |
De-Mold Time: 6-8 hrs |
3M Scotchcast™ 2130 Flame-Retardant Compound 3M Scotchcast Flame-Retardant Compound 2130 is a two-part polyurethane resin designed to replace the cable jacket when splicing or repairing mine and portable cables. Its unique formulation makes it.. |
|||
Cure Time | >= 2160 min @Temperature 0.000 °C |
>= 36.0 hour @Temperature 32.0 °F |
De-Mold Time: 6-8 hrs |
3M Scotchcast™ 2131 Flame-Retardant Compound 3M Scotchcast Flame-Retardant Compound 2131 is a two-part polyurethane resin designed to replace the cable jacket when splicing or repairing mine and portable cables. It formulation makes it particu.. |
|||
Cure Time | 2160 min @Temperature 25.0 °C |
36.0 hour @Temperature 77.0 °F |
Full Chemical |
Chesterton MRS 10 Metal Rebuilding System Description: A reinforced composite for the repair and protection of metal surfaces. It is machinable with excellent compressive strength, chemical resistance It is non-sagging, non-shrinking and 10.. |
|||
Cure Time | 2160 min @Temperature 16.0 °C |
36.0 hour @Temperature 60.8 °F |
Full Load |
Chesterton MRS 58 Metal Rebuilding System An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 1.5 mm (60 mils) or mo.. |
|||
Cure Time | 2160 min @Temperature 25.0 °C |
36.0 hour @Temperature 77.0 °F |
Full Chemical |
Chesterton MRS 58 Metal Rebuilding System An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 1.5 mm (60 mils) or mo.. |
|||
Cure Time | 2160 min @Temperature 32.0 °C |
36.0 hour @Temperature 89.6 °F |
Full Chemical |
Chesterton MRS 58 Metal Rebuilding System An advanced ceramic composite for the repair and protection of all metal surfaces subjected to erosion, corrosion and chemical attack. It is normally applied at a thickness of 1.5 mm (60 mils) or mo.. |
|||
Cure Time | 2160 min @Temperature 25.0 °C |
36.0 hour @Temperature 77.0 °F |
Overcoat End |
Chesterton ARC S1HB Sprayable high-viscosity, 100% solids, advanced coating An advanced composite formulated to protect concrete and metal surfaces from corrosion and chemical attack. It is normally applied at a thickness of 1-2 mm (40-80 mils) per coat. However, greater si.. |