Processing Properties | Metric | English | Comments |
---|---|---|---|
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | |
Plastcom PLASTAMID® 6 GF 25 002 PA6 reinforced with glass fiber PA 6 for injection molding, reinforced with 25% glass fiber, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools, .. |
|||
Injection Pressure | 80.0 - 110 MPa | 11600 - 16000 psi | |
Plastcom PLASTAMID® 66 GF 20 PA66 reinforced with glass fiber PA66 for injection molding, reinforced with 20% glass fiber, for moldings used in the automotive, electrical, building, engineering and hobby industry - holders of electric hand tools, hobby tools, .. |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Zhejiang Juner PC-A2-1 Top-Grade Flame Retardant UV-Resistant Applications: Top-Grade Wall Switch, BracketInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Zhejiang Juner PC-A2-9A Top-Grade Flame Retardant UV-Resistant Applications: Top-Grade Wall Switch, BracketInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Zhejiang Juner PC-A5 Top-Grade Flame Retardant UV-Resistant Applications: Top-Grade Wall Switch, BracketInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Zhejiang Juner PC-A7-5 Top-Grade Flame Retardant UV-Resistant Applications: Top-Grade Wall Switch, BracketInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 CF40 Polyamide 6 40% Carbon Fiber - Antistatic and Electroconductive Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Electroconductive grade based on carbon fiber reinforcement, very high stiffn.. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 CFHI Polyamide 6 - Antistatic and Electroconductive Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Electroconductive grade based on carbon fiber reinforcement, very high stiffn.. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 GF10 MX6 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grade, reinforced with 10% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning, good surface quality.T.. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 GF40 I Polyamide 6 - Glass Fiber Reinforced 40% Glass fiber reinforced, impact modified, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following mai.. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 GF50 Polyamide 6 - Glass Fiber Reinforced 50% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High.. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 MCS I Polyamide 6 - Impact Modified High impact resistance grade. Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:H.. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 MCS I8 Polyamide 6 - Impact Modified Increased impact resistance grade. Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main propert.. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 Polyamide 6 - Natural Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High mechanical strength, rigidi.. |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Beijing Chemical Industry KAIFA® 201-G30R PBT Resin 30% glass fiber reinforced, good flow and toughnessInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Beijing Chemical Industry KAIFA® 301-G10F PBT Resin 10% glass fiber reinforced, flame retardant, good flow, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Beijing Chemical Industry KAIFA® 301-G30RF PBT Resin 30% glass fiber reinforced, flame retardant, good toughness, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | injection speed: 80 - 120 rpm |
Beijing Chemical Industry KAIFA® GL1200 ABS General Purpose Grade Middle impact, Good mechanical strength, High flexural strengthInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | injection speed: 80 - 120 rpm |
Beijing Chemical Industry KAIFA® GL2100 ABS Good Flow Grade Good flow, Easy processing, High glossInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Beijing Chemical Industry KAIFA® HN301-G30 PA6 Resin 30% glass fiber reinforced, flame retardantInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Beijing Ranger Chem PBT 403 M-G30 HF Halogen Free Flame Retarding FR PBT Modified PBT Characteristics: Unreinforced grades have abundant strength and flexibility, and have strong characteristics against brittleness. UL-certified slow-burning (94HB) and self-extinguishin.. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 GF15 Polyamide 6 - Glass Fiber Reinforced 15% Glass fiber reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following main properties:High.. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 MCS 850 Polyamide 6 - Flame Retarded, Unreinforced Glow wire resistance 850°C, bromine and red phosphorus free, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has .. |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Beijing Chemical Industry KAIFA® 201-G30 PBT Resin 30% glass fiber reinforcedInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Beijing Chemical Industry KAIFA® 301-G20F PBT Resin 20% glass fiber reinforced, flame retardant, good flow, low bleedingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | injection speed: 80 - 120 rpm |
Beijing Chemical Industry KAIFA® GL5100 ABS Extrusion Grade Non-toxic, Superior impact strength at low temp., High gloss, Uniform sheet thickness for vacuum moldingInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Injection Pressure | 80.0 - 120 MPa | 11600 - 17400 psi | |
Beijing Chemical Industry KAIFA® HN201-G10 PA6 Resin 10% glass fiber reinforcedInformation provided by Beijing Chemical Industry Research Institute (Group) |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 GF10 GB20 Polyamide 6 - Glass Beads Reinforced 10% Glass fiber and 20% glass beads reinforced, medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Tarnamid® has the following .. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 GF25 FRV0 Polyamide 6 - Flame Retarded, Reinforced Flame retarded grades, flammability class V0, reinforced with 25% glass fibers, without addition of any halogen compounds, red phosphorus and asbestos, doesn't release any toxic gases during burning.. |
|||
Injection Pressure | 80.0 - 130 MPa | 11600 - 18900 psi | 80 MPa is recommended |
Azoty Tarnow™ Tarnamid® T-27 GF25 M Polyamide 6 - Improved Slip Properties Medium viscosity injection molding grade, also used for compounding, for production of monofilament, bristles and fibers.Low wear and low friction grade, contains molybdenum disulfide, PTFE.Tarnamid.. |