Processing Properties | Metric | English | Comments |
---|---|---|---|
Processing Temperature | 650 °C | 1200 °F | Typical Firing Temperature |
Ferro EG 3600 Metal Sealing Glass Type: Si-Ba Alkali Typical Powder Form: VSD Typical Application: Compress.Ferro Metal Sealing glasses are formulated for sealing a wide range of metal packages and parts, including matched se.. |
|||
Processing Temperature | 649 - 760 °C | 1200 - 1400 °F | Brazing Temperature |
Lucas-Milhaupt Silvaloy® 50 Brazing Alloy Silvaloy is one of the lower melting brazing alloys composed of silver, copper, zinc and cadmium. It is suitable for use on most metals except aluminum and magnesium. It is used for joining steel, s.. |
|||
Processing Temperature | 649 °C | 1200 °F | Preheating Temp. |
Wieland Portadur T Casting Alloy Gold casting alloyApplications: inlays/onlays, crowns, acrylic veneeringDental |
|||
Processing Temperature | 649 °C | 1200 °F | Brazing, <15 minutes |
Cadi 1 MOLD-MOR™ A very hard heat treatable copper alloy with moderate electrical conductivity. C18000 offers excellent value for the properties it offers. C18000 is a viable substitute for C17500 and C17510 for m.. |
|||
Processing Temperature | 649 °C | 1200 °F | Brazing, <15 minutes |
Cadi 10 MOLD-MOR™ A Copper Nickel Silicon Chromium Alloy with high thermal conductivity and moderate hardness.Information provided by Cadi Company. |
|||
Processing Temperature | 649 °C | 1200 °F | Brazing, <15 minutes |
Cadi 150 Copper Alloy A small addition of Zr to copper improves resistance to softening and resists deformation at high temperatures where normal copper would soften rapidly. Zirconium copper is used as a Class 1 electr.. |
|||
Processing Temperature | 649 °C | 1200 °F | Brazing, <15 minutes |
Cadi 162 Copper Alloy Cadmium addition to copper increases hardness and resistance to softening. C16200 is utilized in numerous applications where fatigue strength and high electrical conductivity are required. Cadmium.. |
|||
Processing Temperature | 649 °C | 1200 °F | Brazing, <15 minutes |
Cadi 1815 Copper Alloy Zirconium addition to chromium copper improves creep resistance at high operating temperatures and reportedly reduces sticking of electrodes to the work during spot welding of galvanized materials. .. |
|||
Processing Temperature | 649 °C | 1200 °F | Brazing, <15 minutes |
Cadi 182 Copper Alloy Chromium copper is the primary copper alloy used for resistance spot and seam welding. This alloy achieves good hardness and electrical conductivity through a combination of heat treatment and cold .. |