- Polymer Property : Processing Temperature = 25.0 °C
Polymer Property : Processing Temperature = 25.0 °C Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 25.0 °C | 77.0 °F | Curing Agent Temperature |
| Northstar Polymers MGB-A90A High Performance Polyurethane Cast Elastomer System 90A This is a PTMEG/MDI base high-performance polyurethane casting system. This system is recommended to applications in which the part requires high rebound, slide abrasion, constant water contact and.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Curing time: 16 hours; Postcure: 2 hours/100°C (212°F) |
| Abatron AboCast 8-13/Abocure 8-13 Epoxy
(discontinued **) 2-part, clear, solvent-free dielectric epoxy casting compound.Processing: 100/12.80 ratio (pbw); Gel time, 100 g (3.5 oz.): 53 minutes; cures in 16 hours at 25°C (77°F); postcure: 2 hours at 100°.. |
|||
| Processing Temperature | 25.0 - 27.0 °C | 77.0 - 80.6 °F | Average value: 26.2 °C Grade Count:13 |
| Overview of materials for Silicone, RTV, Construction Grade This property data is a summary of similar materials in the MatWeb database for the category "Silicone, RTV, Construction Grade". Each property range of values reported is minimum and maximum values.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure Schedule: 7 days @ 25°C |
| Huntsman HY 3100 Aromatic Amine Approx. H+ equivalent weight 55. Mix Ratio with GY 6010 is 23.Comments/Applications: High solids coatings, floorings and tank linings. Good acetic acid resistance and other aggressive environment.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure Schedule: 7 days @ 25°C |
| Huntsman HY 3441 Phenalkamine Hardener Approx. H+ equivalent weight 130. Mix Ratio with GY 6010 is 40.Comments/Applications: Low temperature cure coatings with excellent corrosion and moisture resistance. Cure can go down to 0°C. .. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure Schedule: 7 days @ 25°C |
| Huntsman HZ 3441 OU-66 Phenalkamine Hardener Approx. H+ equivalent weight 190. Mix Ratio with GY 6010 is 50.Comments/Applications: Low temperature cure coatings with excellent corrosion and moisture resistance. Cure can go down to 0°C. .. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure Schedule: 7 days @ 25°C |
| Huntsman HZ 9795 W-75 Aromatic Amine Approx. H+ equivalent weight 77. Mix Ratio with GY 6010 is 30.Comments/Applications: High solids coatings, floorings and tank linings. Good acetic acid resistance and other aggressive environment.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | 40 - 60 minute film cure |
| Fibre Glast 182 White Gel Coat #182 White Gel Coat is a highly durable ISO gel coat and is the industry production standard for molding applications. Use as a sandable base coat for painting or polish to a high luster finish. Spr.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure Schedule: 7 days @ 25°C |
| Huntsman XU 442 Phenalkamine Hardener Approx. H+ equivalent weight 125. Mix Ratio with GY 6010 is 40.Comments/Applications: Low temperature cure coatings with excellent corrosion and moisture resistance. Cure can go down to 0°C. .. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Momentive Performance Materials RTV109 Aluminum Adhesive Sealant, High Strength Paste One-part acetoxy cure. Acetoxy cure silicones are the most commonly used type of RTV materials and are considered GE Silicones' general purpose product line. Typical uses: High strength high perfo.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure time 24 hrs. |
| Momentive Performance Materials RTV12 Clear General Purpose Potting/Encapsulating Compound Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Momentive Performance Materials RTV162 White Adhesive Sealant, Non-Corrosive Paste One-part totally non-corrosive alkoxy cure. Alkoxy cure silicones are neutral cure materials that offer exceptional adhesion and are non-corrosive to most metals. Typical uses: Non-corrosive bindi.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Momentive Performance Materials RTV167 Gray Adhesive Sealant, Non-Corrosive High Strength One-part totally non-corrosive alkoxy cure. Alkoxy cure silicones are neutral cure materials that offer exceptional adhesion and are non-corrosive to most metals. Typical uses: Highest strength ad.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure time 24 hrs. |
| Momentive Performance Materials RTV41 White General Purpose Potting/Encapsulating Compound Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Momentive Performance Materials RTV6802 White Adhesive Sealant, Industrial Plastic Adhesive One-part modified alkoxy cure. Modified alkoxy materials cure at room temperature and will outgas a small amount of ammonia and some alcohol during cure. Typical uses: Primerless adhesion to many .. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Momentive Performance Materials RTV6803 Black Adhesive Sealant, Industrial Plastic Adhesive One-part modified alkoxy cure. Modified alkoxy materials cure at room temperature and will outgas a small amount of ammonia and some alcohol during cure. Typical uses: Primerless adhesion to many .. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Momentive Performance Materials RTV6809 Aluminum Adhesive Sealant, Industrial Plastic Adhesive One-part modified alkoxy cure. Modified alkoxy materials cure at room temperature and will outgas a small amount of ammonia and some alcohol during cure. Typical uses: Primerless adhesion to many .. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure time 24 hrs. |
| Momentive Performance Materials RTV8111 White General Purpose Potting/Encapsulating Compound Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure time 24 hrs. |
| Momentive Performance Materials RTV8262 Red General Purpose Potting/Encapsulating Compound Two-part condensation cure. Two-part condensation cure silicones RTVs are designed to cute at room temperature, and can be applied at temperature up to one inch (2.5 cm). These are very tough mate.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Momentive Performance Materials RTV5812 White Adhesive Sealant, Fast Cure Paste One-part modified alkoxy cure. Modified alkoxy materials cure at room temperature and will outgas a small amount of ammonia and some alcohol during cure. Typical uses: Fast-curing primerless adhes.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Momentive Performance Materials RTV5813 Black Adhesive Sealant, Fast Cure Paste One-part modified alkoxy cure. Modified alkoxy materials cure at room temperature and will outgas a small amount of ammonia and some alcohol during cure. Typical uses: Fast-curing primerless adhes.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Momentive Performance Materials RTV5818 Translucent Adhesive Sealant, Fast Cure Paste One-part modified alkoxy cure. Modified alkoxy materials cure at room temperature and will outgas a small amount of ammonia and some alcohol during cure. Typical uses: Fast-curing primerless adhes.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure time 5 min. |
| Momentive Performance Materials RTV6126 Clear Potting/Encapsulating Gel Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depth.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure time 4 hours. |
| Momentive Performance Materials RTV615 Clear General Purpose Potting/Encapsulating Compound Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depth.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | Cure time 4 hours. |
| Momentive Performance Materials RTV656 Clear Extreme Low Temperature Potting/Encapsulating Compound Two-part addition cure. Two-part addition cure RTV silicones can be cured very quickly with the use of high heat. Addition cure products have no cure by-products and can be used to unlimited depth.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Momentive Performance Materials RTV6703 Black Adhesive Sealant, General Purpose Paste One-part modified alkoxy cure. Modified alkoxy materials cure at room temperature and will outgas a small amount of ammonia and some alcohol during cure. Typical uses: General purpose adhesive sea.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Momentive Performance Materials RTV6708 Translucent Adhesive Sealant, General Purpose Paste One-part modified alkoxy cure. Modified alkoxy materials cure at room temperature and will outgas a small amount of ammonia and some alcohol during cure. Typical uses: General purpose adhesive sea.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Abatron AboCast/AboCure 8109-13 Liquid hardener version of AboCast/AboCure 8109-11.Processing: 100/23 pbw; Potlife: 3-5 h/20°C (68°F), 1-3 h/40°C (105°F), 0.5-1 h/60°C (140°F); mix at RT; cures in: 30 mins/60°C (140°F), 45.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Abatron AboCast/AboCure 8109-8 All-purpose, structural dielectric resin. High thermal and chemical resistance and RT cure.Processing: 100/12 ratio; Potlife: 45 min/20°C (68°F), 20 min/40°C (105°F), 10 min /60°C (140°F); mi.. |
|||
| Processing Temperature | 25.0 °C | 77.0 °F | |
| Abatron AboCast/AboCure 8109-9 Minimum toxicity version of 8109-8.Processing: 100/25 ratio; Potlife: 45 min/20°C (68°F), 20 min/40°C (105°F), 10 min /60°C (140°F); mix at RT; cures in: 24 h/20°C (68°F), 2-3 h/60°C (140°.. |
|||