- Polymer Property : Processing Temperature = 170 °C
Polymer Property : Processing Temperature = 170 °C Product List
Processing PropertiesTips: 30 items are displayed at most. For the rest of the results, please contact customer service.
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 170 - 175 °C | 338 - 347 °F | Plasticizing Zone |
| Petroquimica Triunfo Trithene® TS 4016 LDPE and LLDPE Blend - Film The Trithene® TS 4016 resin is a mixture of low-density polyethylene (LDPE) with linear low-density polyethylene (LLDPE) designed to meet the needs of the technical films segment for the use of aut.. |
|||
| Processing Temperature | 170 - 180 °C | 338 - 356 °F | Plasticizing Zone; Coextrusion with polyamide |
| Petroquimica Triunfo Trithene® TS 7006 LDPE - Coextruded Film The Trithene TS 7006 resin is a low-density polyethylene (LDPE) with high molecular weight and very good clarity. The unique combination of good processability, bubble stability, gloss, and strength.. |
|||
| Processing Temperature | 170 - 230 °C | 338 - 446 °F | |
| PolyChem Alloy PolyBlaz 7525PM An Antimicrobial Agent Masterbatch. |
|||
| Processing Temperature | 170 - 185 °C | 338 - 365 °F | Mixture Zone |
| Petroquimica Triunfo Trithene® TX 3003 LDPE - Shrink Wrap Film The Trithene® TX 3003 resin is a low-density polyethylene (LDPE) with high molecular weight, presenting excellent mechanical properties. The product provided elevated gloss and transparency, adding.. |
|||
| Processing Temperature | 170 - 193 °C | 338 - 379 °F | Average value: 180 °C Grade Count:7 |
| Overview of materials for Epoxy, Molded, Mineral Filled This property data is a summary of similar materials in the MatWeb database for the category "Epoxy, Molded, Mineral Filled". Each property range of values reported is minimum and maximum values of .. |
|||
| Processing Temperature | 170 - 185 °C | 338 - 365 °F | Molding temperature |
| Cookson Group Plaskon® 3400 Epoxy Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A reduced-stress epoxy molding compound for the encapsulation of a variety of semiconductor devices ranging from small lead count.. |
|||
| Processing Temperature | 170 - 185 °C | 338 - 365 °F | Molding temperature |
| Cookson Group Plaskon® S-7LA Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.A low stress, low alpha emission molding compound designed for packaging stress-sensitive memory devices. It offers an alpha par.. |
|||
| Processing Temperature | 170 - 185 °C | 338 - 365 °F | Molding temperature |
| Cookson Group Plaskon® SMT-B-1RC (146.403) Epoxy Molding Compound for PBGAs
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.An epoxy molding compound optimized specifically for PBGA applications. It has the same unique resin system as SMT-B-1, which mi.. |
|||
| Processing Temperature | 170 - 185 °C | 338 - 365 °F | Molding temperature |
| Cookson Group Plaskon® SMT-B-1 LAS (146.408) Epoxy Molding Compound for PBGAs
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.An epoxy molding compound optimized specifically for grid arrays (BGA/LGA) requiring low alpha particle count. It is formulated .. |
|||
| Processing Temperature | 170 - 185 °C | 338 - 365 °F | Molding temperature |
| Cookson Group Plaskon® ULS-12LA Molding Compound
(discontinued **) Test specimens were transfer molded and post cured 4 hours at 175°C.An ultra low stress, low alpha emission molding compound designed for packaging stress-sensitive memory devices such as TSOPs and.. |
|||
| Processing Temperature | 170 - 290 °C | 338 - 554 °F | |
| IRPC Polimaxx Polene 1102H Polypropylene Homopolymer CHARACTERISTICS: GOOD STIFFNESS, GOOD EXTRUDABILITY, HIGH IMPACTAPPLICATIONS: MONOFILAMENT/YARN/SHEET EXTRUSION FOR THERMOFORMINGBLOW MOLDING AND INJECTION MOLDING FOR ROPESCOARSE TEXTILE FOR JUMBO .. |
|||
| Processing Temperature | 170 - 190 °C | 338 - 374 °F | Metering Temperature, Extrusion |
| Stellarchem GP-950 TPE Compound This grade of Stellarchem TPE is shear dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It's a soft, elastomeric polyolefin based, complete.. |
|||
| Processing Temperature | 170 - 190 °C | 338 - 374 °F | Metering Temperature, Extrusion |
| Stellarchem GP-980 TPE Compound This grade of Stellarchem TPE is shear dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It's a soft, elastomeric polyolefin based, complete.. |
|||
| Processing Temperature | 170 - 190 °C | 338 - 374 °F | Metering Temperature, Extrusion |
| Stellarchem MP-845B TPE Compound This grade of Stellarchem TPE is shear dependent and can be processed on conventional thermoplastics equipment for injection molding or extrusion. It's a soft, elastomeric polyolefin based, complete.. |
|||
| Processing Temperature | 170 - 210 °C | 338 - 410 °F | Extrusion |
| Total Lotrene® Q2018C Linear Low Density Polyethylene, Blown Film Lotrene® Q2018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer. They are designed for film applications and can be used in pure form .. |
|||
| Processing Temperature | 170 - 210 °C | 338 - 410 °F | Extrusion |
| Total Lotrene® Q2018H Linear Low Density Polyethylene, Blown Film Lotrene® Q2018 Series are Linear Low Density Polyethylene resins produced in a gas phase reactor using butene (C4) co-monomer. They are designed for film applications and can be used in pure form .. |
|||
| Processing Temperature | 170 - 230 °C | 338 - 446 °F | |
| Zhejiang Juner JEPP2007 PP For Automotive Parts Applications: Inner Decorate PartsInformation provided by Zhejiang Juner New Materials Co, Ltd. |
|||
| Processing Temperature | 170 - 210 °C | 338 - 410 °F | |
| ELASTO UK Dryflex® 400801S SBS Based Material, 80A Hardness, Natural The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for.. |
|||
| Processing Temperature | 170 - 210 °C | 338 - 410 °F | |
| ELASTO UK Dryflex® 420351S SBS Based Material, 35D Hardness, Natural The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for.. |
|||
| Processing Temperature | 170 - 210 °C | 338 - 410 °F | |
| ELASTO UK Dryflex® 420501S SBS Based Material, 50D Hardness, Natural The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for.. |
|||
| Processing Temperature | 170 - 210 °C | 338 - 410 °F | |
| ELASTO UK Dryflex® 422451S SBS Based Material, 45D Hardness, Black The 400S-series is a good alternative for indoor applications and disposable articles that do not have high requirements for ageing and heat resistance. The raw materials are specially selected for.. |
|||
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Daikin DAI-EL G-603 Fluoroelastomer Terpolymer, Bisphenol Curable Grade, 71% Fluorine Content Offers minimal compression set and excellent sealing. The terpolymer type is able to withstand polarized solvents to realize a wide range of application.Information provided by Daikin Industries. |
|||
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Daikin DAI-EL G-751 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Features: General purpose with excellent metal bonding and compression set.Infor.. |
|||
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Daikin DAI-EL G-763 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Features: Excellent mold releasability for O-rings.Information provided by Daiki.. |
|||
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Daikin DAI-EL G-781 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Information provided by Daikin Industries. |
|||
| Processing Temperature | 170 - 240 °C | 338 - 464 °F | Injection molding |
| BASF Elastollan C 65 A HPM TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c.. |
|||
| Processing Temperature | 170 - 240 °C | 338 - 464 °F | Injection molding |
| BASF Elastollan C 70 A HPM TPUR Description: Thermoplastic Polyester Polyurethane Elastomers with excellent mechanical properties and chemical resistance, outstanding wear resistance, high tear and tensile strength, good damping c.. |
|||